din 1.0570 chemical composition
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
High-high quality steels embrace all carbon and alloy steels. They are designated by a 4 digit quantity – from 1.1xxx to 1.89xx, usually with very high and particular purity grades and a low content of phosphorus and sulphur. By definition, software steels, high velocity steels and nitrided steels are therefore excessive-high quality steels.
We can offer you St52-3 sheet, St52-3 Cross Reference, St52-3 Schematic, St52-3 Distributor, St52-3 Equivalent, St52-3 Application Note, St52-3 Data Sheet, St52-3 part, St52-3 Fiche Technique, St52-3 Circuit, St52-3 steel sheet, St52-3 steel price. St52-3 steel provider, St52-3 steel manufacturer, DIN17100 normal ST52-3 steel. Our products have been utilized in all kinds of areas, corresponding to aviation, aerospace, navigation, nuclear power, chemical trade, electronic data, machinery manufacture, petrochemical, automotive, instrument and meter, communication, transportation, and medical devices, and so on. Up to what number of years we will use st52 materials tube in hydraulics, what would be the time interval up to which we can use the material.
S235 and S355 steels are the most well-liked amongst those introduced here, as they cover most needs. S275 doesn’t find a lot use and may be tougher to seek out. Change in hardness, yield strength and UTS of – ResearchGate.
1.0570 steel grade offers quite good cold forming capability however isn’t nicely suited to hardening, except for limited warmth therapy processes. If warmth therapy is undertaken, elements corresponding to furnace kind, component dimensions, rate of heating and cooling ought to all be taken into consideration. Steel grades are categorised by their technical properties and/or by their supposed use.
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
|
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
|
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (product analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
|
0.24 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
|
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
|
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
|
0.22 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
| EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
|
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
|
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
|
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
|
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
|
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
|
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
|
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
|
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
|
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
|
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
|
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
|
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
|
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
|
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
|
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
|
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
|
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
|
St52-3 |
22 |
21 |
20 |
by agreement |
||||
|
St52-3N |
20 |
19 |
18 |
|||||
st52-3 din 1.0570
Q345 metal weldability, chilly & sizzling workability and corrosion resistance are good. Widely utilized in bridges, ships, boilers, stress vessels, petroleum storage tanks, lifting transport machinery and different excessive-load welded structural parts. EN 1.0570 steel DIN 17100 ST 52-3 is a carbon (non-alloy) metal formulated for primary forming into wrought products. Cited properties are applicable for the normalized condition. 1.0570 is the EN numeric designation for this material.
Kloeckner Metals ODS Nederland has a variety of products. The Export division concentrates on the following range of products. Eworld is the world’s largest small-quantity steel provider. We sell a wide variety of metals including Hot-Rolled Steel, Cold-Rolled Steel, Stainless Steel, Alloy Steel, Galvanized Steel Pipe and Oil Tanks.
- Carbon and other components act as hardening brokers, stopping dislocations within the iron atom crystal lattice from sliding past each other.
- Carbon is the most typical alloying material for iron, however numerous different alloying parts are used, similar to manganese, chromium, vanadium, and tungsten.
- Altering the number of alloying elements and the form of their presence within the steel affects qualities such as hardness, ductility, and tensile energy of the resulting steel.
They are extremely alloyed with carbide-forming elements corresponding to chromium, molybdenum, tungsten and vanadium and, alternatively, cobalt for special thermal burdens. In comparability to low-alloy steels, high speed steels are capable of as much as a ten-fold enhance in slicing velocity, as they’ve very excessive temperature energy, put on resistance, resistance to tempering and thermal hardness . They are additionally known as HSS-Steels (e.g. PREMIUM 1. AISI/SAE M 2).
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price