st52-3 din
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
st52-3 vs c45
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
The St52 layer of composites confirmed the microhardness value of ~190 HV whereas the initial St52 sheet had a microhardness round one hundred sixty HV. The composite produced by the traverse pace of 70 mm/min had the very best yield and supreme tensile power. This high strength achieved with no remarkable lower in elongation because of the formation of a heterogeneous microstructure. The fracture surfaces indicated that the bonding between IF and St52 steels in the composites produced by traverse speeds of 70 and a hundred mm/min was high sufficient robust to maintain integrity as much as a high degree of deformation in the course of the tensile check. Finally, with growing the tool traverse velocity, the dimensions and depth of dimples decreased.
The chemical composition for A513 is generally iron with added carbon, manganese, phosphorus, silicon, and silver. Check out the chart beneath for actual A513 carbon metal chemical specifications. Welding dissimilar metals by fusion welding is difficult. Friction stir welding as a stable-state joining technique can overcome these issues.
The most hardness within the stir zone reached as much as about 347 HVdue to the strong state transformations and grain refinement. The welded plates displayed an final tensile energy of about 389 MPa, which lies between the final word tensile strength of St37 and St52 steels, 373 and 526 MPa, respectively. Moreover, the yield power of the dissimilar joint was discovered to be about 272 MPa, which is also between those of the base plates joined.
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
|
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
|
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (product analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
|
0.24 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
|
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
|
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
|
0.22 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
| EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
|
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
|
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
|
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
|
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
|
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
|
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
|
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
|
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
|
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
|
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
|
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
|
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
|
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
|
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
|
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
|
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
|
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
|
St52-3 |
22 |
21 |
20 |
by agreement |
||||
|
St52-3N |
20 |
19 |
18 |
|||||
EN Mechanical Properties of Precipitation Hardening EN is the fabric commonplace for stainless steel sheet, plate and strip for general purposes. This article gives the 0.2% proof power, tensile power , yield strength and elongation ranges, where specified, of the DIN 17100 ST 52-3 two precipitation hardening grades listed in the usual. ST 52-3 steel grade is a low carbon, excessive energy structural steel. With this low carbon equal, it course of good chilly forming property. ST 52-3 metal plates traditional provided in normalized or management rolled supply condition.
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
In the current research, a brand new composite together with interstitial free metal as the outer layer and St52 because the internal layer was fabricated by friction stir lap welding . The microstructures and mechanical properties of initial and composite samples were investigated. It was discovered that the standard of interfacial bonding for the software traverse speeds of 70 and a hundred mm/min was glorious as a result of higher strain price. It was observed that the microstructure of composite samples consisted of nice equiaxed ferrite, Widmanstatten ferrite, martensite, grain boundary ferrite, and aggregates of ferrite + cementite. The improve of software traverse speed from 40 to 70 and a hundred mm/min at a constant tool rotation pace of one thousand rpm decreased the cooling time leading to the next cooling rate and the formation of martensite section.
The outcomes present that a defect-free Ti-15-3 alloy weld joint may be successfully fabricated by the FSW. The materials flow field within the SZ reveals an incline of ~ 10° towards the advancing aspect across the welding path .
- In the present analysis, a new composite together with interstitial free steel because the outer layer and St52 as the inner layer was fabricated by friction stir lap welding .
- The grain measurement of the composite produced by the traverse velocity of forty mm/min in the first and second HAZ areas was bigger than that of the 70 mm/min because of the greater warmth enter and due to this fact lower cooling fee of the pattern welded by 40 mm/min.
- It was discovered that the quality of interfacial bonding for the software traverse speeds of 70 and one hundred mm/min was glorious due to the higher pressure price.
- The microstructures and mechanical properties of initial and composite samples had been investigated.
- The enhance of device traverse pace from 40 to 70 and one hundred mm/min at a constant device rotation velocity of 1000 rpm decreased the cooling time leading to the next cooling rate and the formation of martensite part.
The results obtained point out that the weld region is comprised of advanced microstructures corresponding to Widmanstatten ferrite, ferrite with or without carbide aggregates and grain boundary ferrite. The maximum hardness within the stir zone reached as much as about 347 HV as a result of solid state transformations and grain refinement. The yield strength of the joint was discovered to be about 272 MPa.
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price