st52-3 density
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
The migration of the iron atoms occurs at very slow cooling speeds. They tackle a new reticular association (γ → α) and, at the similar time, the carbon atoms migrate to form the cementite. This transformation product known as pearlite (ferrite + cementite).
- Sub-crucial spheroidizing This heat treatment just isn’t beneficial for hypoeutectoid steels C ≤ 0.eighty three% to be machined with chip removing, however it is the solely remedy which can make hypereutectoid steels C 0.832.06% machinable.
- Stress-free annealing This is carried out at a temperature of between 580 °C and 650 °C, with cooling in a furnace down to °C earlier than being discharged into air.
- Cooling (about 10 °C/hour, usually 5-10 °C/minutes for carbon steels and °C/hour for alloy steels) may be carried out both in a furnace or in air.
- This therapy does not modify the construction however adequately softens and eliminates the stresses as a result of previous processes.
- It is a wonderful warmth therapy for materials for use for cold forming and extrusion.
- It is carried out at a temperature close to to Ac1 (–10 °C) but they have to be held at this temperature for lengthy durations, 1 hour for every 10 mm of thickness of the bundle of bars or rolled or cast products of the complete load.
st 52-3 vs s355
These fittings are to be used in stress piping and in pressure vessel fabrication for service at reasonable and elevated temperatures.MatWeb The Online Materials Information ResourceData sheets for over 135,000 metals, plastics, ceramics, and composites. The search phrase you entered, st37 2, is widespread to 2 materials, by searching on the time period [ “st37 2”] in commonest textual content fields, . Results are displayed up to a most of 200 supplies per page. Follow the links beneath to view complete property information. Calculation of important factors on the basis of the chemical composition of the steel expressed in %.
In follow, it is used to find out the hardness trend in pieces hardened with industrial strategies. The take a look at is carried out on a pattern obtained from the product of a particular cast which is heated in a particular furnace until reaching the austenitization temperature after which quenched by a water spray, in order to obtain managed cooling propagation along the sample axis. The sample must endure normalization therapy earlier DIN 17100 ST 52-3 than the test. A collection of hardness tests is then carried out from the hardened floor , starting from 1 mm and normally reaching 50 mm, so as to get hold of the decreasing curve. Part three • Technical tables Full annealing Heating at a temperature of °C above the important range Ac3 for hypoeutectoid steels, Ac1 for hypereutectoid steels, pause at this temperature for a suitable time, 2-3 minutes each mm of thickness of the part to be handled.
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
|
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
|
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (product analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
|
0.24 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
|
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
|
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
|
0.22 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
| EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
|
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
|
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
|
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
|
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
|
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
|
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
|
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
|
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
|
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
|
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
|
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
|
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
|
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
|
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
|
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
|
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
|
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
|
St52-3 |
22 |
21 |
20 |
by agreement |
||||
|
St52-3N |
20 |
19 |
18 |
|||||
st52-3 round bar equivalent
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
0.50-0.57 0.15-0.35 0.forty-0.70 ± 0.03 ± 0.03 ± 0.04 Permissible deviations on the product. Suitable for products to be additional scorching-shaped. Suitable for products to be additional processed . The tempering temperature is dependent upon the required hardness.
Sulphocarbonitriding Heat and chemical remedy so as to improve the sulphur, carbon and nitrogen content on the surface. Tempering This is the heat therapy which a ferrous product undergoes after hardening by quenching, to attain the specified mechanical properties.
This finish allows the restoration of the mechanical properties after chilly processing. Products with good ductility and specific magnetic properties. Products used of their current situation or meant for better ending.
Spheroidizing Geometrical change of carbide particles, similar to plates of cementite, towards a secure spherical form. Stress relieving Treatment to reduce stresses with out lowering hardness. It is usually carried out at 50 °C below the final tempering carried out on the components that are set in operation with high strength. The cooling must be notably gradual, generally in a furnace.
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price