1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
The additional put on safety of a floor treatment may be added, with out sacrificing deformation resistance. The CPM grades present wonderful substrates for all sorts of floor remedies. Because of their excessive hardness, vanadium carbides are significantly helpful for wear resistance. When present in vital quantities, vanadium carbides tend to dominate other types in affecting wear properties. For instance, M4 high pace metal’s chemical content is nearly identical to M2 high pace metal, besides M4 accommodates four% vanadium instead of two%.
In addition, the uniformity of the CPM microstructure provides improved toughness in CPM versions of standard tool steels. The CPM variations of the identical grades are extra proof against brittle failures. In fact, most CPM grades designed for metalforming tools have impression resistance similar to the decrease put on resistance grades similar to D2.
- An understanding of these properties, combined with an understanding of what elements restrict device life for a specific software (breakage, put on, deformation, and so on.), will permit software users to specify the most effective performing grade for almost any software.
- In reality, the same properties would be necessary to think about in carbide materials in addition to steels.
- Each of those properties could also be varied independently in device steels to some extent, so it makes sense to contemplate each separately.
Different tool steels are used at comparable hardnesses, but offer important differences in expected put on life. Thus, hardness just isn’t usually a major think about put on resistance, solely in deformation resistance.
Because the microstructural distribution of carbides in P/M steels is so fine and uniform, higher quantities of carbide-forming components may be added. Thus, greater put on resistance could also be developed, with out the toughness and grindability limitations inherent in standard steelmaking. The P/M process has allowed the event DIN 17100 ST 52-3 of grades containing four%, 5%, 10%, and even 15% vanadium, providing far larger put on resistance than conventionally produced software steels. Because of their high put on resistance, these high vanadium P/M grades are significantly appropriate for top production operations.
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
st52-3 chemical composition
What is MS grade steel?
Mild steel is a type of carbon steel with a low amount of carbon – it is actually also known as “low carbon steel.” Although ranges vary depending on the source, the amount of carbon typically found in mild steel is 0.05% to 0.25% by weight, whereas higher carbon steels are typically described as having a carbon
Tools for stamping metal typically must be about 56/fifty eight HRC minimal, though some form instruments, and instruments for non-ferrous work materials, could also be softer. Most device steels are capable of reaching roughly comparable hardness levels (low 60’s HRC), and thus will have related abilities to resist plastic deformation. However, some excessive pace steels, similar to CPM Rex T15 and Rex seventy six, can achieve hardnesses approaching 70 Rockwell C. Keep in mind that in software steels, the most important mechanism controlling put on properties is the sort and quantity of carbide particles present. For this reason, rising the hardness just isn’t generally an efficient technique for increasing the wear lifetime of tools, but just for minimizing deformation.
When coatings aren’t practical, materials providing a mixture of excessive toughness, high hardness, and resistance to abrasion, corresponding to CPM 3V or CPM M4, are instructed. Most of those coatings are applied at temperatures of about 850/1050F. Thus, the therapy process can limit the service hardness of low or medium alloy steels. However, the higher alloy content steels similar to M2, M4 as well as CPM 3V, 9V, 10V, 15V retain their most hardness after such exposures. Thus, regular floor remedy temperatures don’t have any effect on their hardness, and tools may be treated with out fear of dimensional or hardness modifications.
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
Chemical Composition (product analysis), %, ≤ |
|||||||||||
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
0.24 |
30 <d ≤100 |
||||||||||
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
0.24 |
30 <d ≤100 |
||||||||||
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
0.24 |
30 <d ≤100 |
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
0.22 |
30 <d ≤100 |
||||||||||
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
0.22 |
30 <d ≤100 |
||||||||||
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
0.22 |
30 <d ≤100 |
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
Elongation (≥, %); Thickness (d), mm |
||||||||
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
Elongation (≥, %); Thickness (d), mm |
||||||||
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
St52-3 |
22 |
21 |
20 |
by agreement |
||||
St52-3N |
20 |
19 |
18 |
However, they generally do not present the extent of performance needed for prime volume manufacturing. Specifically, the place lengthy runs and rare regrinding are desired, other greater alloy device steels or carbide could be used to improve from these tool steels. Traditionally, different properties, corresponding to influence resistance, may be sacrificed to be able to acquire the higher put on properties. Conversely, steels chosen for his or her resistance to impact or breakage may not be capable of high put on resistance. An understanding of those software metal properties and related issues permits selection of the optimum steel for many applications.
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price