Standard: EN 10025-6:2004, European standard for hot-rolled structural . Part 6 – Technical delivery conditions for flat products of high yield structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

Based on the given results, recommendations for correlation components βw have been delivered by the statistical evaluation carried out in accordance with . Due to the noticed correlation between the load bearing capacity and the stress scenario of the weld, a willpower of correlation elements βw relying on the stress state of affairs is beneficial.

EN 10025-6 S690Q strength steel microstructure

Base Materials

The approach was applied to S355 structural metal bulk samples as well as an autogenously electron beam welded pattern the place there is a native variation of fabric properties. This electrode produces a deposit characterized by an distinctive hardness and resistance to abrasion, mixed with moderate impact. Deposit essentially composed of complex carbides of Cr and Nb, in an austenitic matrix. Good resistance to mineral abrasion and impression as a result of very fine presence of Nb carbides.

Welding parameters, cooling price and so forth. were chosen following the recommendations for welding of metallic materials based on EN . All welding procedure parameters e.g. wire feeding rate, welding present, welding voltage, welding speed etc. had been properly documented in a big information base with entry given in . In order to get a power function, the test specimens have been designed in order to initiate failure within the weld. Details of the fracture surface, including the weld root penetration and the angle of fracture had been measured at various places alongside the weld length.

Used on 18/8 stainless steels for service temperatures from –196 °C up to +350 °C. Austenitic chrome steel electrode, fundamental kind coating with approx. Used on 18/eight stainless steels (304H- type) for elevated service temperatures up to + 750°C.

The most impact vitality value of 26 J was obtained from the only-side-welded pattern, which is bigger than these obtained from the double-aspect-welded samples . Many extra dislocations and plastic deformations had been found in the fusion zone than the warmth-affected zone in the joint, which hardened the joints and lowered the influence toughness.

Influence Of Heat Treatment On The Mechanical Properties Of An Fe E 460 Tmcp Steel

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

无标题文档

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade

Standards

Country

S690QL EN10137-2 EN10025-6:2004

EN

EUROPE

A709-100

ASTM

USA

TStE690V DILLIMAX 690 NAXTRA 70

DIN, WNr

GERMANY

E690T E690TFP S690T

AFNOR/ NF A36- 204

FRANCE

FeE690VKT

EN

EUROPEAN (OLD)

2625 WELDOX 700

SS

SWEDON

E690

ISO 4952

INTER

JFE HITEN 780LE

JIS

JAPAN

ALFORM 700

AUSTRIA

mechanical properties of grade EN10025-6 S690Q

 

Minimum yield strength – ReH
MPa

Tensile strength Rm
MPa

Minimum elongation – A
Lo = 5,65* √So (%)

Steel grade

Nominal thickness
mm

Nominal thickness
mm

 

>3
≤50

>50
≤100

>100
≤150

>3
≤50

>50
≤100

>100
≤150

S690Q

690

650

630

770-940

760-930

710-900

14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature
°C

-20

0

Min. absorbed energy
J

40

50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature
°C

-40

-20

0

Min. absorbed energy
J

27

30

35

The tables below show the chemical composition of grade EN10025-6 S690Q

 

Ladle analysis.
Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties.
Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.

Steel grade

C
max.
%

Mn
max.
%

Si
max.
%

P
max.
%

S
max.
%

B
max.
%

Nb
max.
%

V
max.
%

Ti
max.
%

Cr
max.
%

Mo
max.
%

Ni
max.
%

Cu
max.
%

Mo
max.
%

N
max.
%

Zr
max.
%

CEV
max. %

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

≤50

>50
≤100

>100
≤150

S690QL

0,20

1,70

0,80

0,020

0,010

0,005

0,06

0,12

0,05

1,50

0,70

2,0

0,50

0,70

0,015

0,15

0,65

0,77

0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old
EU 137 (1983)

France
AFNOR

Sweden
SS

Germany
DIN,WNr

FeE 690 V KT

E690T

2625

TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

Versatile flux for joint welding and surfacing with appropriate strong or flux-cored wire electrodes of stainless CrNi-types, mainly austenitic- and DUPLEX-qualities, or Ni-base-alloys. Based on the chosen uncooked-supplies the weld deposits achieved with the flux BF 25 are impartial with respect to Mn, Si and other alloying components such as Cr and Ni. The flux is appropriate for SAW of butt and fillet welds, mainly fin-to-tube wall fillet welds, with single and multiple wire processes (for instance TWIN-ARC). Smooth weld bead appearance with flat weld interfaces and self deslagging with out slag residuals, are other special features of BF 25. Uniform mechanical and chemical property performance make BF 25 flux appropriate for a lot of SAW-applications in the stainless and heat-resistant steel fabrication.

Used for repairing and joining of Nickel alloys, 5 % Nickel steels, cryogenic stainless steels (right down to –196°C), Incoloy 800 and different excessive temperature steels. For joining dissimilar supplies as stainless steels to low alloyed steels, stainless steels to Nickel alloys, for buttering of inauspicious to weld steels. Deposit insensitive to cracks, superb resistance towards acids, salt and alkaline solutions, molten salt. A extremely fundamental, agglomerated flux with a chemical composition and a production methodology, which ensures virtually neutral metallurgical reactions.

  • Though the impairment of the mechanical performance of welds can not be avoided and utterly eradicated, it may be decreased by producing a very narrow warmth affected zone that adjoin to the weld.
  • It is possible by welding with an utilization of laser or high-energy electron beams.
  • The software of excessive-energy beams is associated with melting solely a narrow zone of welded metals and excessive-price heating followed by excessive-fee cooling occurring in warmth affected zone.
  • In this case much less warmth, comparing to conventional arc welding, is launched to the welded metals.
  • This high-price thermal cycle results from very small beam interacting quantity.
  • The excessive heating fee affect the homogenization of austenite whereas high cooling rate the precipitation processes.

Most current evaluation of nano-indentation check data assumes the pattern to behave as an isotropic, homogeneous body. This heterogeneity results EN10025-6 S690Q steel plate supplier in considerable scatter within the indentation load-displacement traces and complicates inverse evaluation of this knowledge.

The experimental design for lap joints included duplicated tests in all circumstances. For chosen test specimens a further equivalent check specimen was fabricated for accompanying exams. For cruciform and butt joints, in every case 8 identical check samples were out there. A restricted variety of 34 specimens were tested at low temperature (-40 °C) to analyze the fracture behaviour of welded connections at severe service circumstances.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.