en 10025-6 s890ql m s steel plate weight calculator manufacturer

Gangsteel Sell EN 10025-6 S890QL Extra High Strength Steel Plate and export EN10025-6 S890QL Quenched and Tempered Structural Steel IN China.What is EN 10025-6 Grade? S890QL Grade Designation , S = Structural Steel, 890 = minimum yield strength (MPa), Q = Quenching & Tempering and L = Low notch toughness testing temperatures

es

s890ql DNV BV GL LR steel plate,s890ql steel equivalent,s890ql steel plate,s890ql mechanical properties,s890ql properties,s890ql datenblatt,s890ql steel price,s890ql schweißen,en 10025-6 s890ql,welding s890ql,s890ql steel cutting parts,s890ql chemical and property,acier s890ql,s890ql werkstoff,s890ql hardness,s890ql equivalent,s890ql werkstoff datenblatt,s890ql datasheet,acciaio s890ql,s890ql material,blacha s890ql,s890ql steel stocklist,s890ql equivalent,s890ql equivalent steel,s890ql steel equivalent,s890ql steel platesteel plate,en 10025-6 s890ql steel plates manufacturer,en 10025-6 s890ql weight of steel plate manufacturer,en 10025-6 s890ql steel plate weight manufacturer,en 10025-6 s890ql steel plate prices manufacturer

We recommend to consult us prior to the first working with DILLIMAX 1100. For scorching rolled steels, it is strongly recommended to make use of a filler metal with the identical energy or with only barely larger energy than the base material.

en 10025-6 s890ql steel plate weight calculator manufacturer,en 10025-6 s890ql steel plate for sale manufacturer,en 10025-6 s890ql steel plate 1/4 manufacturer,en 10025-6 s890ql steel plate armor manufacturer,en 10025-6 s890ql steel plate thickness manufacturer,en 10025-6 s890ql steel plate 1/8 manufacturer,en 10025-6 s890ql steel plate 3/16 manufacturer,en 10025-6 s890ql 3/16 steel plate manufacturer,en 10025-6 s890ql 1/8 steel plate manufacturer,en 10025-6 s890ql steel name plates manufacturer,en 10025-6 s890ql steel plate on road manufacturer,en 10025-6 s890ql steel plate 1/2 manufacturer,en 10025-6 s890ql steel plate sizes manufacturer,en 10025-6 s890ql 1/2 steel plate manufacturer

Plate thicknesses and dimensions which deviate from the standard dimensional program for this steel grade, could also be possible on request. DILLIMAX 890 may be chilly fashioned with regard to its high yield power. Finally, it’s the fabricator’s duty to obtain the required values of the steel by way of an appropriate heat therapy. Those favorable properties are being achieved by software program of particular procedures of thermo-mechanical processing and simultaneous alloying with enough elements.

en 10025-6 s890ql steel plate 3/8 manufacturer

Cold forming of DILLIMAX 890 should be carried out according to the next suggestions. It is preferentially used for welded metal constructions within mechanical constructions, plant constructions and structural steel works, corresponding to machines for structural engineering, conveying crops, hoists, cranes, flood gates, bridges and frameworks.

For larger chilly forming quantities we suggest you to seek the advice of the steel producer previous to ordering. To regain the initial properties new quenching and tempering become necessary. However, water quenching of a fashioned workpiece or part will usually be less efficient than the original quenching within the plate mill in order that the fabricator may not have the ability to reestablish the properties required and due to this fact hot forming is probably not suitable. In this respect we recommend you to contact the metal producer previous to ordering, in all instances where scorching forming is required.

en 10025-6 s890ql steel plate 6mm price manufacturer

Delivery conditions of s890q, s890ql, and s890ql1 steel plates. Quenching + tempering (q). Note: direct quenching followed by tempering after hot rolling is equivalent to conventional quenching and tempering.6. Impact properties of s890q, s890ql, and s890ql1 steel plates and S890q at – 20 ��, s890ql at – 50 ��, s890ql at – 60 ��

S890QL is extra high strength steel to EN10025-6:2004, and the steel number is 1.8983. S890QL has a minimum yield strength of 890Mpa in quenched and tempered conditions; with its low temperature of -40 ºC, this steel grade performs good durability in extreme working environments.

In these cases the weld metal is alloyed via a dilution with the base plate, which has a strengthening effect on the weld metal. The benefit of undermatching welding consumables is that the formability and toughness of the weld metallic is improved in comparison with matching consumables. The alternative of filler metal for boron metal is determined by whether the welding is carried out earlier than heat remedies or solely after hardening and, probably, tempering.

• It is able to improve the performance, sturdiness, and security of cars, lifting tools, and metal structures.
• In order to ensure that the tensile strength of the weld metal fulfils the requirements of the base steel, the warmth input and interpass temperature have to be limited throughout welding.
• Fast supply and good after-sales service are also out there.
• For common welding directions, please seek the advice of the EN 1011.
• Experience has proven that the welding circumstances must be chosen so that the cooling time t 8 / 5 doesn’t exceed 20 seconds.

en 10025-6 s890ql 1/8 steel plate near me manufacturer

Henan HZZ provides a large selection of top quality JIS G3106 SM490A carbon and low-alloy excessive-energy metal plate with N. The entire processing and software strategies are of elementary significance to the reliability of the merchandise produced from this metal. The user ought to ensure that his design, development and processing methods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply with and are suitable for the supposed use. The buyer is answerable for the selection of the fabric.

Having been focused on varied metal products for over 20 years, we now brings customers quality merchandise with excessive precision and excessive power. Fast delivery and good after-gross sales service are also out there. For general welding directions EN10025-6 S890QL Steel supplier, please consult the EN 1011. In order to make sure that the tensile power of the weld metallic fulfils the requirements of the bottom steel, the warmth enter and interpass temperature have to be limited during welding.

Consumables for climate-resistant steels must be selected in the way in which that the welds become weathering. Nickel and copper are the most common alloy parts in weathering filler metals. Unalloyed filler steel may be used where the joint design and the degree of penetration (submerged arc weld-ing) present ample blending of the bottom material into the weld metallic. In such cases, the weld steel takes up the weathering alloying parts from the molten base material. In multi-run welding, the ultimate runs ought to always be made with weathering filler metallic.

en 10025-6 s890ql steel plates Mechanical Properties

Plate Thickness MM	Yield Strength ReH(Mpa)	Tensile Strength Rm(Mpa)	Elongation A5% Minimum
3 to 50	890	940~1100	11
> 50 to 100	830	880~1100	11

Technical conditions for s890q, s890ql and s890ql1 steel plates
1. S890 steel plate is a quenched and tempered high strength steel plate with series grades of s890q, s890ql and s890ql1. It is a low carbon non alloy structural steel plate with European standard en10025-6. It can be produced by Wuyang Iron and steel company in China. In order to ensure its performance, the carbon content of this kind of steel plate is less than 0.2%.
2. S890q, s890ql and s890ql1 steel plates, where s means structural steel, Q means impact temperature of steel plate is – 20 ° C,Then QL means the impact temperature of the steel plate is – 50 ° C. guess what ql1 stands for, ql1 means the impact temperature of the steel plate is – 60 ° C, 890 means the minimum yield strength value specified by the thickness of (50 mm),
Chemical Composition – EN 10025-6 S890QL. Content % (ladle analysis), maximum.

C	SI	MN	P	S	B	CR	CU	MO
0.20	0.80	1.70	0.020	0.010	0.005	1.50	0.50	0.70
N	NB*	NI	TI*	V*	ZR*
0.015	0.06	2.0	0.05	0.12	0.15

EN 10025-6 s890ql steel plates V Notch Impact Test

Position of Samples	0 ºC	-20 ºC	-40 ºC
Longitudinal	50 Joules	40 Joules	30 Joules
Transverse	35 Joules	30 Joules	27 Joules

en 10025-6 s890ql steel plates Quenched and Tempered Structural Steel

Minimum recommended inside bending radius
Axis of bend in transverse direction 3.0t	Axis of bend in longitudinal direction 4.0t

3. The steel specified in this standard can be used for the production of hot rolled plate with minimum nominal thickness of 3 mm and maximum nominal thickness of less than 150 mm for S460, S500, S550, S620, s690, S890 and s960 series steel plates. The minimum yield strength specified for Quenched and tempered steel is 460mpa1) to 960 mpa1)
4. Production size; Thickness; 6-300mm, width max 3800mm length.
en 10025-6 s890ql Chemical Composition

C	Si	Mn	P	S	B	Cr	Cu	Mo
0.20	0.80	1.70	0.020	0.010	0.005	1.50	0.50	0.70
N	Nb*	Ni	Ti*	V*	Zr*
0.015	0.06	2.0	0.05	0.12	0.15

PLATE THICKNESS MM	YIELD STRENGTH REH (MPA)	TENSILE STRENGTH RM (MPA)	ELONGATION A5 % MINIMUM	IMPACT STRENGTH J, MINIMUM
3 to50	890	940 – 1100	11	30 @ -40º C
50to 100	830	880 – 1100	11	30 @ -40º C

en 10025-6 s890ql steel plates manufacturer and property Chemical Properties Of s890ql steel plate:

C

Si

Mn

Ni

P

S

Cr

Mo

V

N

Nb

Ti

Cu

Zr

B

CEV

max   0.2

max   0.8

max   1.7

max   2

max   0.025

max   0.015

max   1.5

max   0.7

max   0.12

max   0.015

max   0.06

max   0.05

max   0.5

max   0.15

max   0.005

max   0.82

Mechanical Properties Of s890ql steel plate:

Designation		Mechanical Properties (ambient temperature)
Steel Name	Steel Number	Min. Yield Strength Reh MPa			Tensile Strength Rm MPa			Min. % elongation after fracture
		Nominal thickness (mm)			Nominal thickness (mm)
		≥3 ≤50	≥50 ≤100	≥100 ≤150	≥3 ≤50	≥50 ≤100	≥100 ≤150
S890QL	1.8983	890	830	––	940/1100	880/1100	––	11

Notch Impact Energy:

Grade	Sample Orientation	@ 0°C	@-20°C	@-40°C	@-60°C
S890QL	Longitudinal	50 J	40 J	30 J	––
	Traverse	35 J	30 J	27 J	––

1.Grade:
S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

2. Specification:
  Thickness: 8mm to 300mm
   Width: 1500mm to 4200mm
   Length: 4000mm to 18000mm

3. Adopt Standard: EN10025-6 2004

4. Heat Treatment: Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technology, etc.

5. Delivery Time: 30-40days

6. Payment Item: 30% TT, or LC and TT.

7..Trade Terms: FOB, CFR, CIF

8. Steel Services: Cutting, Painting, Pretreatment, and The third party inspection in DNV, BV, LR, ABS, SGS ,etc and others in super thick ship steel plate.

Gangsteel is specialized in super thick low alloy, high strength steel plate and cooperated with ABS, BV, DNV, CCS, GL, LR, KR, NK, and RINA Classification Society to approve the super thickness plate to 300mm now.
If you have any inquiry in steel price or technical conditions, please contact us freely.

s890ql werkstoff datenblatt

The energy of filler metals for pressure equipment steels, how-ever, should meet the necessities of a energy coefficient for stress tools. The use of overmatching filler metals results in high residual stresses.

The standard specifies seven steel grades, and their yield strength at ambient temperature is different. All steel grades to be supplied in the following steps shall be established when required. The specified minimum value of impact energy when the weather is not lower than – 20 �� (no label). When the temperature is not lower than – 50 ��, the specified minimum value of impact energy is expressed in L. (except for s960), the minimum amount of impact energy set when the temperature is not lower than – 60 �� is defined as L1. In quenching and tempering delivery conditions (q) and grade L: Steel en 10025-6-s460ql; or steel en10025-6-1.8906.