st52-3 material mechanical properties
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
Stainless steel is now used as one of the supplies for tramlinks, along with aluminium alloys and carbon steel. Duplex grades are typically most well-liked due to their corrosion resistance and better energy, allowing a reduction of weight and an extended life in maritime environments.
What is the difference between s275 and s355?
S275 provides a lower strength (than S355) but has good machinability and can be welded. The average minimum yield for S275 steel is 275 N/mm² giving its name: S275. BS EN 10025 S355, S355JR, S355J2 and S355J2+N supercedes BS4360 50A, 50B, 50C 50D.
The identical grades exposed to stronger bases corresponding to sodium hydroxide at high concentrations and excessive temperatures will doubtless experience some etching and cracking. Increasing chromium and nickel contents present increased resistance. Replacing some carbon in martensitic stainless steels by nitrogen is a latest growth.[when?
The ensuing iron oxide surface layer is porous and fragile. In addition, as iron oxide occupies a larger quantity than the original metal, this layer expands and tends to flake and fall away, exposing the underlying metal to further assault. This passive movie prevents further corrosion by blocking oxygen diffusion to the metal surface and thus prevents corrosion from spreading into the majority of the steel. This movie is self-repairing, even when scratched or briefly disturbed by an upset situation in the setting that exceeds the inherent corrosion resistance of that grade.
The minimum 10.5% chromium in stainless steels offers resistance to approximately seven hundred °C (1,300 °F), whereas 16% chromium offers resistance as much as roughly 1,200 °C (2,200 °F). Type 304, the most common grade of chrome steel with 18% chromium, is resistant to roughly 870 °C (1,600 °F).
st52-3 ekvivalent
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
Chemical Composition (product analysis), %, ≤ |
|||||||||||
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
0.24 |
30 <d ≤100 |
||||||||||
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
0.24 |
30 <d ≤100 |
||||||||||
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
0.24 |
30 <d ≤100 |
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
0.22 |
30 <d ≤100 |
||||||||||
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
0.22 |
30 <d ≤100 |
||||||||||
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
0.22 |
30 <d ≤100 |
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
Elongation (≥, %); Thickness (d), mm |
||||||||
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
Elongation (≥, %); Thickness (d), mm |
||||||||
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
St52-3 |
22 |
21 |
20 |
by agreement |
||||
St52-3N |
20 |
19 |
18 |
The plates can be found in several sorts, shapes, sizes, thicknesses, lengths, specs, varieties, finishes, dimensions, diameters, and so forth. The plates can be found in several varieties like hot and cold rolled plates, polished plates, and so DIN 17100 ST 52-3 forth. India commonplace 2062 grade E350C is utilized in manufacture the plates and due to this grades the particular property increases. The grades E350C have many features like glorious resistance property, strength, and so forth.
- Moreover, stainless-steel can be rolled into sheets, plates, bars, wire, and tubing.
- Resistance to different gases relies on the kind of gasoline, the temperature, and the alloying content material of the chrome steel.
- Type 304, the commonest grade of stainless-steel with 18% chromium, is proof against approximately 870 °C (1,600 °F).
- Other gases, such as sulfur dioxide, hydrogen sulfide, carbon monoxide, chlorine, also assault stainless steel.
Like metal, stainless steels are comparatively poor conductors of electrical energy, with significantly lower electrical conductivity than copper. In explicit, the electrical contact resistance of stainless steel arises as the results of the dense protecting oxide layer, and limits is performance in functions as electrical connectors . Copper alloys and nickel coated connectors are inclined to exhibit lower ECR values, and are most popular materials for such purposes. Nevertheless chrome steel connectors are employed in situations with ECR poses a lower design standards and corrosion resistance is required, for example in high temperatures and oxidizing environments . The addition of chromium remains the most typical methodology to increase excessive-temperature corrosion resistance in stainless steels; chromium reacts with oxygen to type a chromium oxide scale, which reduces oxygen diffusion into the fabric.
Is 2062 material yield strength?
These standard is 2062 gr A Mild plates offer high tensile and good yield strength, good mechanical strength, ductility, hardness, and toughness. These plates show high toughness at high temperatures and rust-free.
din 1.0570 chemical composition
Austenitic stainless-steel is the most important household of stainless steels, making up about two-thirds of all chrome steel manufacturing . They possess an austenitic microstructure, which is a face-centered cubic crystal structure.
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price