1.0570 zerspanbarkeit
st52-3 steel specification
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
Cylindrical grinding in HEDG mode has also been carried out based on the knowledge obtained from the surface grinding. It has shown that the HEDG know-how could be transferred efficiently to the sphere of cylindrical grinding to realize very excessive specific materials DIN 17100 ST 52-3 removal charges in excess of 400mm3/mm.s. The successful application of HEDG to cylindrical elements depends on the appropriate choice of grinding parameters and likewise the grinding fluid provide strategy.
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
|
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
|
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (product analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
|
0.24 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
|
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
|
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
|
0.22 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
| EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
|
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
|
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
|
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
|
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
|
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
|
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
|
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
|
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
|
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
|
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
|
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
|
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
|
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
|
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
|
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
|
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
|
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
|
St52-3 |
22 |
21 |
20 |
by agreement |
||||
|
St52-3N |
20 |
19 |
18 |
|||||
On the draw back, break of 1.5271 assist will indicate that the down development from 2.1161 is finally resuming for a brand new low below 1.3503. Nevertheless, break of 1.6746 will invalidate this view and would likely deliver stronger rally to 1.7043 resistance and above.
Though, the stable Q3 GDP knowledge seemed to have lowered the urgency for the Fed to do one thing in November and FOMC could just save the bullet for Q1 subsequent yr. Nonetheless, markets should search for affirmation to the chance of QE3 to increase latest threat rally. In addition, there were proposals for Fed to explicitly specific that it’s going to hold the coverage price at ultra low level till both unemployment drops beneath 7% or medium term inflation expectation rises above 3%. FOMC may incorporate related things in the assertion.
If the 1.3950 stage exhibits resistance, and we do fall below 1.3895, we would even be breaking beneath the channel seen within the 4H chart. This breakout opens up the 50% retracement of the 1.3138 to 1.4246 rally, at 1.3690. 1.3680 is a assist cluster together with the 200SMA and assist seen in the consolidation from Oct. thirteen-21, as well as resistance on Oct. 10. So the 1.3680-1.37 space could possibly be a target for a break beneath 1.3895. EUR/GBP’s rebound from 0.8529 resumed last week and reached as excessive as 0.8830, just ahead of 61.eight% of 0.8529 to 0.8796 from 0.8669 at 0.8834, before forming a temporary prime there.
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
Below 0.87, the first areas of assist are 0.8670 low from final week, and the 0.8650 pivot seen in the day by day chart. Note the failure in the RSI studying in the daily chat to return back above 60, and thus reflecting a spread-sure momentum. The current bearish outlook subsequently is in the quick-term within context of a ranging market in the medium time period. The bearish state of affairs ought to be considered if as a substitute of assist, the market slides via the 1.3950 pivot, then additionally the 200 interval simple transferring common and also the 1.
- In addition, there have been proposals for Fed to explicitly categorical that it’s going to maintain the policy rate at ultra low level till both unemployment drops below 7% or medium time period inflation expectation rises above 3%.
- That is, ought to Fed disappoint and dent the hope on further quantitative easing, we would very doubtless see a deep pull back in risk as a substitute.
- Nonetheless, markets ought to look for affirmation to the prospect of QE3 to extend recent threat rally.
- FOMC may incorporate comparable things within the assertion.
But another rise will remain in favor so long as 0.9865 assist holds. Much volatility was seen in USD/JPY final week but the pair’s rally try was restricted at 77.forty eight. Also, there isn’t a observe via buying to help USD/JPY maintain above close to time period falling development line yet. More uneven sideway trading might be seen between 76.eleven and 77.48 initially this week.
Break there ought to pave the way to 1.0764 resistance and above. On the downside, under 1.0104 minor assist will turn bias impartial and bring consolidations.
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price