güte st 52-3
1.0570 Material,St52-3 Steel Equivalent,st52-3,st52.3,st52.3n,st 52-3 n,st52-3n,st52-3 material,st52-3 equivalent,st52-3 equivalent grade,st 52-3 neue bezeichnung,st52-3k,st52-3 chemical composition,steel st52-3,st52.3 steel,st52-3 material equivalent,st52-3 steel,st52-3 datenblatt,st52-3 equivalent in indian standard,st52-3 steel equivalent,steel st52-3 equivalent,st52-3 material properties,st52-3 grade specification,1.0570 st 52-3,st52-3 odpowiednik,din st52-3,din st52.3,st52-3 werkstoffnummer,st52-3n material properties,st52-3n material,st52-3 u,st52-3 steel plate,st52.3 tube,werkstoff st52-3,st52-3 material specification,st52-3 tube,st52-3 eigenschappen,st52-3 equivalent sae,st52-3 plate,st52-3 steel equivalent astm,st52-3 steel chemical composition,st52-3 hardness,st52-3 jis
gangsteel produced and exported DIN 1.0570 and ST 52-3 steel plate as common carbon structural steel. Gangsteel supply DIN17100 ST52-3 ST52-3N Steel plate low alloy and high strength steel plate. DIN 17100 ST52-3 steel plate price and stock supplier.ST 52-3 steel plate is one mainly of Carbon structural steel, ST 52-3 is a type of steel sheet under DIN standard which is used to build ship, bridge, belongs to high strength sheet.
If you have any requirement for ST 52-3 structure steel plate,under DIN17100 standard ST 52-3 steel plate, under DIN17100 standard, please contact us.
1.Steel Grade : ST 52-3 (1.0570)
2. Standard: DIN 17100 steels for general structural purposes
3. Approval By Third Party :ABS, DNV, GL, CCS, LR , RINA, KR, TUV, CE
4. Classification: General structural purposes
5. Product form : super heavy steel plate
The outcomes have demonstrated the feasibility of FSW of metal with acceptable tensile properties. Based on these results, FSW of transformation-hardenable steels, HSLA steels, and stainless steels appears feasible. The effect of stir depth on joint efficiency was additionally determined. A grain refinement in addition to evolution of a Widmanstätten structure was achieved throughout the stir zone of all the joints produced. S355J2+N steel stockholders and suppliers, delivering to the whole of the India.
ST52-3 metal is principally a low alloy and excessive power structural steel that may be welded with different weldable steels. These steel plates are available in different sizes and shapes as per the demand and requirement of shoppers. Due to the low carbon current, the steel possesses good corrosion resistance and chilly forming properties.
equivalent of 1.0570
- Comparisons before and after welding combining both metallographic and metrology techniques recommend adjustments in software dimensions stem from each rubbing wear and deformation of the software.
- Axial device hundreds measured during FSW were approximately bf (18.7 kN), whereas measured torques were within the range of 500 in.-lb (55 N-m).
- Peak surface temperatures near 1000degreesC had been measured on the workpiece and power throughout welding using thermocouples and an infrared camera system.
- Microstructures of the welds have been examined using optical and scanning electron microscopy.
The S355 steel specs are excessive yield non alloy steels. The common minimal yield for this materials is 355 N/mm², hence the name S355 (with the ‘S’ giving reference to it being a structural metal). This paper deals for the primary time with the results of further cooling medium by submerging underwater on the feasibility of dissimilar bond formation between aluminum and metal in strong DIN 17100 ST 52-3-state throughout friction-stir welding process. Thermo-mechanical cycles in the course of the FSW process are monitored as well as the sound-ness of produced dissimilar weldments by way of supplies inter-mixing, grain structural features, potential part transformations , mechanical property, and subsequent fracture behavior.
1.0570 rohr
Al-alloys are widely used in the transportation industries because of their low density and excellent formability properties. These alloys, that are problematic in fusion-welding processes, can be successfully joined by friction-stir welding.
1.0570 und 1.0577,1.0570 rohr,1.0570 jis,1.0570+c,1.0570 din,1.0570 c45,1.0570 china,steel 1.0570 chemical composition,1.0570 material chemical composition,1.0570 density,din 1.0570 equivalent astm,en 1.0570 equivalent,en 1.0570 properties,s355j2g3 (1.0570) en 10025,1.0570 equivalent jis,din 1.0570 equivalent,din 1.0570 steel,1.0570 material composition,din 1.0570 chemical composition,1.0570+ar,1.0570 equivalent astm material,1.0570 aisi,1.0570 acciaio,1.0570 en 10025,1.0570 material equivalent in india,acero 1.0570 equivalencia,1.0570 bar,1.0570 bestellen,blacha 1.0570,1.0570 bruchdehnung,1.0570 bezeichnung,baustahl 1.0570,e-modul 1.0570,1.0570 fräsen,1.0570 in astm,was ist 1.0570,1.0570 härte hrc,1.0570 h9,1.0570 hrc,1.0570 hot rolled and normalized,jakost 1.0570,1.0570 kerbschlag,1.0570 material specification,1.0570 material density,1.0570 lieferant,1.0570 korrosion,1.0570 kaufen,1.0570 kosten,1.0570 härte,1.0570 heat treatment,1.0570 equivalent grade,steel grade 1.0570 equivalent,1.0570 festigkeit,präzi flachstahl 1.0570,1.0570 geschmiedet,1.0570 gewicht,gatunek 1.0570,1.0570 hardness,1.0570 glühen,1.0570 geschliffen,1.0570 gefüge,1.0570 material spec,
DIN17100 ST52-3 ST52-3N Steel plate Chemical composition of heat analysis:
|
DIN |
ASTM |
EN |
JIS |
Chemical Composition |
C.E. |
||||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
S |
P |
CU |
|||||
|
17100 St52-3N |
A572-50 |
10025-2:2004 S355J2+N |
G3106 SM490YB |
max 0.22 |
max 0.55 |
max 1.60 |
– |
– |
– |
– |
– |
max 0.035 |
max 0.035 |
– |
max 0.047 |
St52-3 steel data sheet – 2, Chemical composition (product analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (product analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.065 |
0.065 |
– |
≤ 30 |
Fully Killded |
|
|
0.24 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.22 |
0.60 |
1.70 |
0.045 |
0.045 |
– |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.22 |
0.60 |
1.70 |
0.035 |
0.035 |
– |
0.60 |
≤ 30 |
||
|
0.24 |
30 <d ≤100 |
||||||||||
St52-3 Steel Properties
Physical Properties
- Material St 52-3 Density: 7.85 g/cm3
- Melting point: 1420-1460 °C (2590-2660 °F)
DIN17100 ST52-3 ST52-3N Steel plate mechanical properties steel plate
|
Thickness (mm) |
Yield Strength Reh min (N / mm2) |
Tensile Strength Rm min (N / mm2) |
Elongation A5 min (%) |
Impact Values Charpy-V-Notch Longitudinal Average from 3 Speimens Thk. >10<150mm. |
|
3<thk<100 |
315-355 |
490-630 |
max 22 |
27 Joules at -20 C |
St52-3 steel data sheet – 1, Chemical composition (ladle analysis) according to DIN 17100 and DIN EN 10025: 1993.
|
Chemical Composition (ladle analysis), %, ≤ |
|||||||||||
|
Country (Region) |
Standard |
Steel Grade (Steel number) |
C |
Si |
Mn |
P |
S |
N |
Cu |
Thickness (d) (mm) |
Method of deoxidation |
|
Germany |
DIN 17100: 1980 |
St52-3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.040 |
0.040 |
– |
≤ 30 |
Fully Killded |
|
|
0.22 |
30 <d ≤100 |
||||||||||
|
European Union |
EN 10025: 1993 |
S355J2G3 (1.0570) |
0.20 |
0.55 |
1.60 |
0.035 |
0.035 |
– |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
|
EN 10025-2: 2004 |
S355J2 (1.0577) |
0.20 |
0.55 |
1.60 |
0.025 |
0.025 |
– |
0.55 |
≤ 30 |
||
|
0.22 |
30 <d ≤100 |
||||||||||
DIN17100 ST52-3 EQUIVALENT STEEL GRADES
| EN 10025 – 2 |
EN 10025+A1 |
?SN |
DIN 17100 |
||
|
EN10027-1 |
EN10027-2 |
EN10027-1 Grade |
EN10027-2 Grade |
|
|
|
S235JR2 |
1.0038 |
S235JRG2 |
1.0038 |
11375 |
RSt 37-2 |
|
S235J0 |
1.0114 |
S235J0 |
1.0114 |
11378 |
St 37-3U |
|
|
– |
S235J2GR3 |
1.0116 |
11378 |
St 37-3N |
|
S235J2 |
1.0117 |
S235J2G4 |
1.0117 |
– |
– |
|
S275JR |
1.0044 |
S275JR |
1.0044 |
11443 |
St 44-2 |
|
S275J0 |
1.0143 |
S275J0 |
1.0143 |
11445 |
St 44-3U |
|
|
– |
S275J2GR3 |
1.0144 |
11448 |
St 44-3N |
|
S275J2 |
1.0145 |
S275J2G4 |
1.0145 |
– |
– |
|
S355JR |
1.0045 |
S355JR |
1.0045 |
11523 |
St 52-3 |
|
S355J0 |
1.0553 |
S355J0 |
1.0553 |
11523 |
St 52-3U |
|
|
– |
S355J2G3 |
1.057 |
11503 |
St 52-3N |
|
S355J2 |
1.0577 |
S355J2G4 |
1.0577 |
– |
– |
Material St 52-3 Datasheet – 3
|
Yield strength (≥ N/mm2); Thickness (d) mm |
||||||
|
Steel (Steel number) |
d≤16 |
16< d ≤40 |
40< d ≤63 |
63< d ≤80 |
80< d ≤100 |
>100 |
|
St52-3 |
355 |
345 |
335 |
325 |
315 |
by agreement |
Tensile Strength
Material St 52-3 Datasheet – 4
|
Tensile strength (≥ N/mm2); Thickness (d) mm |
|||
|
Steel (Steel number) |
d<3 |
3 ≤ d ≤ 100 |
>100 |
|
St 52-3 |
515-680 |
490-630 |
by agreement |
Note: 1MPa = 1N/mm2
Elongation
Material St 52-3 Datasheet – 5
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
0.5 ≤d <1 |
1≤ d <1,5 |
1,5≤ d <2 |
2≤ d <2,5 |
2,5≤ d <3 |
|||
|
St52-3U |
14 |
15 |
16 |
17 |
18 |
|||
|
St52-3N |
12 |
13 |
14 |
15 |
16 |
|||
|
Elongation (≥, %); Thickness (d), mm |
||||||||
|
Steel (Steel number) |
3 ≤d ≤40 |
40< d ≤63 |
63 < d ≤100 |
>100 |
||||
|
St52-3 |
22 |
21 |
20 |
by agreement |
||||
|
St52-3N |
20 |
19 |
18 |
|||||
After the testing process, ST52-3 metal plates are packed in wood cases/ pallets/ cartons with full labeling concerning the product name, its size, and specification and manufacturers particulars. Its correct packaging prevents these metal plates from harm and rust until its last stage of production. CHINA UNITED IRON AND STEEL LIMITED is one of the renowned and notable producers of ST52-3 steel plates, used in numerous purposes due to its admirable features and properties. We are aimed to supply our clients high and superior high quality of plates manufactured beneath the supervision of experts. In addition to it, we make use of high-notch high quality of raw material and take a look at machines for creating an correct dimension and length of plates.
Unitedsteel Plate Factory are specialized in producing and exporting S355J2, S355K2, S355K2 and So on. Low alloy and excessive strength steel plate, heavy plate and extensive, heavy plate, Which is a big steel plate provider mill. Our stock warehouse had about 30000tons S355J2, S355JR, S355K2, S355K4Low alloy steel plates. are specialised in producing and exporting S355J2, S355K2, S355K2 and So on. For all these exams, a number of check certificates are accredited including third-party inspection report, visible inspection report, chemical composition evaluation report and more.
The results present that a defect-free Ti-15-3 alloy weld joint can be successfully fabricated by the FSW. The materials circulate subject throughout the SZ shows an incline of ~ 10° towards the advancing facet around the welding course .
HENAN GANG IRON AND STEEL CO.LTD is a professional super steel plates/sheets manufacture and supplier. We can supply different product type of ST37-2,Ust 37-2 , Rst37-2, ST44-2, ST44-3, ST52-3, ST50-2, ST60-2, ST70-2 .If you have any need of DIN 17100 super heavy steel plate please do not hesitate to contact us .Check St 52.3 Steel Equivalent And Material, Find St52 3 Steel Round Bar Price