S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

In this paper, a series of isothermal and anisothermal elevated temperature exams are performed on two commercially-obtainable metal grades . Following a detailed description of the checks, the results are analysed to find out strength and stiffness discount components EN10025-6 S690Q steel plate supplier at elevated temperatures and these values are compared with literature and EN . It was found that the results for S700MC, for which there is restricted information in the literature, showed better strength retention properties than S690QL at elevated temperatures.

sixteen 2.10.4.2 Mass In general, the deviation in actual mass from mass computed using a density of 7850 kg/m3 shall be restricted by the dimensional tolerances. 2.11 Sheet piles This section covers both scorching rolled and chilly fashioned sheet piles, and interlocking steel pipe piles utilized in earth retaining buildings. Steel bearing piles (see 2.2) and steel pipe piles (see 2.three), except interlocking steel pipe piles used in earth retaining buildings, usually are not inside the scope of this part. NOTE References for material efficiency requirements in this section embody, in alphanumerical order, BS EN , BS EN , BS EN , BS EN 10051, BS EN , BS EN , BS EN and BS EN . 2.11.1 Manufacturing process Rimming steel shall not be allowed and the metal shall be a minimum of semi-killed in the deoxidation process.

无标题文档

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade

Standards

Country

S690QL EN10137-2 EN10025-6:2004

EN

EUROPE

A709-100

ASTM

USA

TStE690V DILLIMAX 690 NAXTRA 70

DIN, WNr

GERMANY

E690T E690TFP S690T

AFNOR/ NF A36- 204

FRANCE

FeE690VKT

EN

EUROPEAN (OLD)

2625 WELDOX 700

SS

SWEDON

E690

ISO 4952

INTER

JFE HITEN 780LE

JIS

JAPAN

ALFORM 700

AUSTRIA

mechanical properties of grade EN10025-6 S690Q

 

Minimum yield strength – ReH
MPa

Tensile strength Rm
MPa

Minimum elongation – A
Lo = 5,65* √So (%)

Steel grade

Nominal thickness
mm

Nominal thickness
mm

 

>3
≤50

>50
≤100

>100
≤150

>3
≤50

>50
≤100

>100
≤150

S690Q

690

650

630

770-940

760-930

710-900

14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature
°C

-20

0

Min. absorbed energy
J

40

50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature
°C

-40

-20

0

Min. absorbed energy
J

27

30

35

The tables below show the chemical composition of grade EN10025-6 S690Q

 

Ladle analysis.
Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties.
Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.

Steel grade

C
max.
%

Mn
max.
%

Si
max.
%

P
max.
%

S
max.
%

B
max.
%

Nb
max.
%

V
max.
%

Ti
max.
%

Cr
max.
%

Mo
max.
%

Ni
max.
%

Cu
max.
%

Mo
max.
%

N
max.
%

Zr
max.
%

CEV
max. %

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

≤50

>50
≤100

>100
≤150

S690QL

0,20

1,70

0,80

0,020

0,010

0,005

0,06

0,12

0,05

1,50

0,70

2,0

0,50

0,70

0,015

0,15

0,65

0,77

0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old
EU 137 (1983)

France
AFNOR

Sweden
SS

Germany
DIN,WNr

FeE 690 V KT

E690T

2625

TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

The outcomes additionally confirmed that under isothermal conditions, the steering for the elastic moduli of these supplies may be unconservative and overly optimistic. 5 NOTE 2 Depending on the product thickness or variation in metallurgical process and supposed use, the requirements for chemical composition would possibly differ and shall be referred to BS EN , BS EN , BS EN , BS EN , BS EN and BS EN . Table 1 — Chemical composition necessities for steel plates based on ladle evaluation Maximum content material (% by mass) py (N/mm2 , based mostly on t sixteen mm) CEV Pa S 235 0.40 0.045 0. 2.1.four Dimensional and mass tolerances 2.1.four.1 Dimensions In general, the deviation in precise thickness from nominal plate thickness shall not exceed the smaller of ± 2 mm and ± 15 %.

2.2.four.2 Mass In general, the deviation in precise mass from mass computed utilizing a density of 7850 kg/m3 shall not exceed ± 6 %, except for T sections where the deviation shall not exceed ± 8 %. 2.3 Hollow sections This section covers each sizzling completed and chilly-formed structural hollow sections of round, sq. or rectangular varieties. Hot finished elliptical hollow sections are additionally within the scope of this part. NOTE References for materials performance requirements in this part embody, in alphanumerical order, BS , BS , BS 7668, BS EN , BS EN , BS EN , BS EN , BS EN and BS EN . 2.three.1 Manufacturing process Rimming steel shall not be allowed and the metal shall be no less than semi-killed in the deoxidation process.

2.9 Stud shear connectors This part covers headed stud shear connectors utilized in transmitting the longitudinal shear between concrete and steel in composite beams and slabs. The shank diameter shall be within the vary of 10 mm to 25 mm. The head diameter shall be no less than 1.5 instances the shank diameter; whereas the top depth shall be no less than 0.4 instances the shank diameter.

A 710 Steel Plate

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

This low alloy steel is meant to symbolize those metal grades where a small addition of vanadium (less than 0.12%) offers enhanced strength over commonplace low C-Mn steels, whereas assembly and even exceeding all requirements for ductility, weldability and toughness. They are normally equipped in the as-rolled or as-solid situation, eliminating the need for subsequent heat treatments.

EN 10025-6 S690Q strength steel young's modulus

Structural Steel Plate

2.4.four Dimensional and mass tolerances 2.four.four.1 Dimensions In general, the deviation in precise thickness from nominal plate thickness shall not exceed the smaller of ± 0.three mm and ± 15 %. 2.four.4.2 Mass In common, the deviation in precise mass from mass computed utilizing a density of 7850 kg/m3 shall be limited by the dimensional tolerances. 2.5 Non-preloaded bolting assemblies This part covers structural bolting assemblies, which embrace the ISO metric hexagon bolts with the matching nuts and washers, used for non-preloaded or bearing kind bolted connections.

HPS can be welded with higher ease than many steels developed up to now . In 1992, AISI partnered with the Carderock Division, Naval Surface Warfare Centre and the Federal Highway Administration to develop new and improved steel alternatives for bridges. The outcome was a brand new sort of steel, known as high-performance metal , which supplied as much as 18% price financial savings and up to 28% weight savings in comparison with conventional metal bridge design supplies. They even have improved fatigue and corrosionresistance properties . 14 2.eight.2 Mechanical properties 2.eight.2.1 Strength The nominal yield energy shall be within the range of 220 N/mm2 to 550 N/mm2 .

  • 2.4.four Dimensional and mass tolerances 2.4.4.1 Dimensions In common, the deviation in precise thickness from nominal plate thickness shall not exceed the smaller of ± 0.three mm and ± 15 %.
  • 9 2.four.2.2 Ductility The elongation after fracture on proportional gauge length shall be a minimum of 15 %, for nominal yield power not larger than 460 N/mm2 ; and shall be a minimum of 10 % for nominal yield power larger than 460 N/mm2 .
  • NOTE Conversion of elongation values measured not based on proportional gauge size is important and shall be carried out according to BS EN ISO .
  • 2.four.3 Chemical composition In general, based mostly on ladle evaluation, carbon content shall not exceed 0.25 %, CEV shall not exceed 0.48 % and content of each phosphorous and sulphur shall not exceed 0.05 %.
  • NOTE Depending on the product thickness or variation in metallurgical course of and intended use, the requirements for chemical composition would possibly differ and shall be referred to BS EN , BS EN , BS EN , BS EN and BS EN 10346.

Steel For Press Tools Blanking Of Ultra High Strength Steel Sheet

2.7 Welding consumables This section covers welding consumables, together with electrodes, wires, rods and fluxes, used in arc welding. NOTE References for materials efficiency necessities on this part embrace, in alphanumerical order, BS , BS , BS EN , BS EN ISO 636, BS EN ISO 2560, BS EN ISO 14171, BS EN ISO 14341, BS EN ISO and BS EN ISO 17632. 2.7.1 Mechanical properties The mechanical properties of the all-weld metallic shall be obtained via multi run technique.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.