S690q Steel Mild Steel

S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

For QT steels EN has an option concerning flangeability for materials with a nominal thickness t sixteen mm. For the 5690 grade the minimal bend radius is three.0 times t with the axis of the bend in the transverse direction and 4.0 instances t within the longitudinal path. For TM steels EN has choices relating to flangeability for materials with a nominal thickness t 5 12 mm and roll forming for material with t 5. For the steel grades S420 and S460 the minimum bend radius is four instances t with the axis of the bend in the transverse course and 5 occasions t in the longitudinal path. For normalized or normalized rolled grades with minimal Ref; 460 MPa the maximum stress reduction temperature must be 560°C.

EN 10025-6 S690Q strength steel vs mild steel

Benefits Of High Strength Steel Plate

S690QL1 plates supply colossal corrosion resistance, rugged metal our bodies that don’t crack or dent, superior payload, and so forth. For TM-material up to S460M it was shown that a superficial heating up to 950°C does not influence the mechanical properties significantly, whereas for more severe heating conditions up to the middle of the plates a most of seven-hundred°C should be noticed. The materials manufacturer must be contacted if more detailed information is required. Table 4 offers examples of the chemical compositions of S460ML, S460QL, and S690QL compared to the common European constructional steel S355J2.

HSLA metal plate Special plate dimensions, together with thicknesses of as much as 200 mm and widths of up to 3,950 mm.

  • About sixty two% of these are steel sheets, 1% are stainless-steel sheets.
  • For constructional steelwork even plates of a hundred and twenty mm have been produced and utilized efficiently in particular in bridges.
  • Alibaba s690q steel delicate steel offers 219 s690q metal plate merchandise.
  • These excessive toughness values additionally end in good welding properties as described under. However, as far as chemical and mechanical properties of the defined steel grades are concerned, these components don’t show massive adjustments compared to the former requirements EN and 10137. Gangsteel sincerely hope new and old clients may inquiry our metal plates. • Shovel and Cranes, their booms and their varieties like tower crane, moveable crane, cable crane and truck mounted crane are heavy weight lifters, resulting in their production by S690QL1, SUPERELSO 690, EN FeE690VKT, grade metal plates, light in weight and carry the extra load.

    Construction of buildings, bridges, towers and other buildings demand equipment and machines which might be inordinately rigid and rugged. If buckets, bulldozers, cranes, trucks, loaders, and so EN10025-6 S690Q steel plate supplier forth. are made of EN S690QL1, EN S690Q, ALDUR 700 Q and other alternates of S690QL1 steel plates, it will catalyse the speed of building.

    DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

    S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

    En10025 6 S500ql High Strength Steel Plate By Xinsteel

    无标题文档

    S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
    Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

    Grade

    Standards

    Country

    S690QL EN10137-2 EN10025-6:2004

    EN

    EUROPE

    A709-100

    ASTM

    USA

    TStE690V DILLIMAX 690 NAXTRA 70

    DIN, WNr

    GERMANY

    E690T E690TFP S690T

    AFNOR/ NF A36- 204

    FRANCE

    FeE690VKT

    EN

    EUROPEAN (OLD)

    2625 WELDOX 700

    SS

    SWEDON

    E690

    ISO 4952

    INTER

    JFE HITEN 780LE

    JIS

    JAPAN

    ALFORM 700

    AUSTRIA

    mechanical properties of grade EN10025-6 S690Q

     

    Minimum yield strength – ReH
    MPa

    Tensile strength Rm
    MPa

    Minimum elongation – A
    Lo = 5,65* √So (%)

    Steel grade

    Nominal thickness
    mm

    Nominal thickness
    mm

     

    >3
    ≤50

    >50
    ≤100

    >100
    ≤150

    >3
    ≤50

    >50
    ≤100

    >100
    ≤150

    S690Q

    690

    650

    630

    770-940

    760-930

    710-900

    14

    EN10025-6 Notch impact test.
    Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

    EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

    Temperature
    °C

    -20

    0

    Min. absorbed energy
    J

    40

    50

    Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

    Temperature
    °C

    -40

    -20

    0

    Min. absorbed energy
    J

    27

    30

    35

    The tables below show the chemical composition of grade EN10025-6 S690Q

     

    Ladle analysis.
    Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties.
    Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.

    Steel grade

    C
    max.
    %

    Mn
    max.
    %

    Si
    max.
    %

    P
    max.
    %

    S
    max.
    %

    B
    max.
    %

    Nb
    max.
    %

    V
    max.
    %

    Ti
    max.
    %

    Cr
    max.
    %

    Mo
    max.
    %

    Ni
    max.
    %

    Cu
    max.
    %

    Mo
    max.
    %

    N
    max.
    %

    Zr
    max.
    %

    CEV
    max. %

     

     

     

     

     

     

     

     

     

     

     

     

     

     

     

     

    ≤50

    >50
    ≤100

    >100
    ≤150

    S690QL

    0,20

    1,70

    0,80

    0,020

    0,010

    0,005

    0,06

    0,12

    0,05

    1,50

    0,70

    2,0

    0,50

    0,70

    0,015

    0,15

    0,65

    0,77

    0,83

     

    EN10025-6 S690Q Steel Grade Equivalent Table

    European old
    EU 137 (1983)

    France
    AFNOR

    Sweden
    SS

    Germany
    DIN,WNr

    FeE 690 V KT

    E690T

    2625

    TStE690V

    Description by Manufacturer
    Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
    EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

    1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

    2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

    3. Adopt Standard: EN 10025-6.

    4. Heat Treatment:
    Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

    5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

    6. Payment Item: 30% TT, or LC and TT

    7. Trade Terms: FOB, CFR, CIF

    8. Delivery Time: 30-40days

    Significant achievements concerning strength, financial system, design versatility, fabrication and erection strategies and service efficiency wouldn’t have been possible without the substantial enhancements of excessive energy steel plate. Especially with the application of “new” manufacturing processes for carbon steels such because the thermo-mechanical rolling and the quenching and tempering course of, excessive power steel plate with good fabrication properties similar to weldability was launched into the development market. S690Q is excessive yield power structural steels grade in the quenched and tempered. because the welding warmth enter increase up to 30.9kJ/cm, the modifications of microstructure and impact toughness were small. At the warmth input of 44.8kJ/cm, nevertheless, toughness decreased obviously as a result of coarsening of coarse-grained HAZ and formation of ferrite at bainite grainboundary of weld metal.

    In November 2004 the brand new commonplace for decent-rolled metal products for usage in steel construction EN was published. This standard has six components and defines the most common structural steel grades which were previously handled in the impartial standards EN and EN 10137.

    S690q,S690ql,S690qql1,S890q,S890ql,S960q_stock_steel_plate

    Reference is made to EN ISO 1461 and EN ISO or to particular chemical requirements in the requirements, see Table 7. These limits concern the thickness and appearance of the zinc layer.

    Menu

    The result is to place toughness and ductility again in to the metal and, although some of the yield energy of the quenched metal is misplaced, the tip results of the quenching and tempering process is to provide a robust metal which is also simple to weld, bend, and fabricate generally. DILLIMAX 690 is a high energy quenched and tempered, nice grained structural steel with a minimal yield energy of 690 MPa 2 in its supply condition . DILLIMAX 690 is preferentially used for welded metal structures inside mechanical constructions, plant constructions and structural steel works, corresponding to machines for structural engineering, conveying plants, hoists, cranes, flood gates, bridges and frameworks. Gangsteel export high yield energy EN S690Q quenched and tempered steel plate.BS EN S690Q structural metal sheet stock Supplier. This paper presents the analysis of the influence of temperature on mechanic properties of the base materials and welded joints manufactured from high power steel.

    Sell steel gradeS690Q steel plate, S690QL metal plate, S690QL1 metal plate . S690QL is good weld ability, 40 temperature influence take a look at in 30J in quenched and tempered metal. The symbol S is structural metal, 690 for the minimal yield strength in thickness under 50mm.EN S690Q quenched and tempered steel plate, BS Victor Steel is one of the Leading Manufacturer, Suppliers of EN S690Q quenched and tempered metal plate, s690q steel plate, in Mumbai,India. Multipurpose Low-Carbon Steel Also generally known as mild steel, multipurpose metal contains low-carbon grades, such as 1018 and A36.

    Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.

    EN 10025-6 S690Q strength steel vs mild steel