S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

The original conclusions on influence of the selected welding process handbook steel arc for the root passes and metal active fuel for the filling and masking passes) on impression toughness of the high-energy low-alloyed steels are drawn. The paper also presents dialogue on the valid standards and recommendations associated to welding of those steels, from the side of applications in design of steel EN10025-6 S690Q steel plate supplier welded constructions. For QT steels EN has an option concerning flangeability for material with a nominal thickness t sixteen mm. For the 5690 grade the minimum bend radius is three.0 occasions t with the axis of the bend within the transverse direction and 4.0 times t in the longitudinal path. For TM steels EN has choices regarding flangeability for material with a nominal thickness t 5 12 mm and roll forming for material with t 5.

• However, this steel has a unfavorable characteristic – proneness to appearance of cold cracks.
• That impedes welding and makes as an imperative to check totally different aspects of this steel’s properties as well as these of eventual filler metal.
• The most distinguished properties are the excessive tensile power and impression toughness, at room and at elevated temperatures, as nicely.
• That metal belongs into a group of steels with distinctive mechanical properties.

Some codes might limit the utmost permissible pressure during cold forming. Depending on the related code this may end up in the need of bigger bending radiuses than indicated in the chart.

With almost 20 years’ experience, Henan HZZ is now generally known as one of the leading producers and suppliers of en s690q carbon and low-alloy high-energy metal plate with pwht. Please rest assured to buy high quality metal products with high power from our manufacturing facility. S690Q is high yield power structural steels grade within the quenched and tempered.

Stress relieving and an abrasive water jet as a substitute of flame chopping could reduce the problem. For TM-materials as much as S460M it was shown that a superficial heating up to 950°C does not affect the mechanical properties considerably, whereas for more extreme heating conditions up to the center of the plates a maximum of 700°C ought to be observed. The materials manufacturer ought to be contacted if more detailed information is needed. Gangsteel sincerely hope new and old prospects might inquiry our steel plates. DILLIMAX 690 is preferentially used for welded steel structures within mechanical constructions, plant constructions and structural metal works, such as machines for structural engineering, conveying crops, hoists, cranes, flood gates, bridges and frameworks.

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Influence Of Heat Treatment On The Mechanical Properties Of An Fe E 460 Tmcp Steel

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

mechanical properties of grade EN10025-6 S690Q

	Minimum yield strength – ReH MPa			Tensile strength Rm MPa			Minimum elongation – A Lo = 5,65* √So (%)
Steel grade	Nominal thickness mm			Nominal thickness mm
	>3 ≤50	>50 ≤100	>100 ≤150	>3 ≤50	>50 ≤100	>100 ≤150
S690Q	690	650	630	770-940	760-930	710-900	14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature °C		-20	0
Min. absorbed energy J		40	50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature °C	-40	-20	0
Min. absorbed energy J	27	30	35

The tables below show the chemical composition of grade EN10025-6 S690Q

	Ladle analysis. Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties. Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.
Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	B max. %	Nb max. %	V max. %	Ti max. %	Cr max. %	Mo max. %	Ni max. %	Cu max. %	Mo max. %	N max. %	Zr max. %	CEV max. %
																	≤50	>50 ≤100	>100 ≤150
S690QL	0,20	1,70	0,80	0,020	0,010	0,005	0,06	0,12	0,05	1,50	0,70	2,0	0,50	0,70	0,015	0,15	0,65	0,77	0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old EU 137 (1983)	France AFNOR	Sweden SS	Germany DIN,WNr
FeE 690 V KT	E690T	2625	TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

This redirection of the crack propagation affected the values of the critical CTOD. Such a sort of welded joint is due to this fact preferable for the welding of high energy low alloy steels, because it enables the manufacturing of a welded joint with out preheating. High energy steel plate grades usually are not supposed for warmth therapy after supply.

Comments

Microstruc-tural examinations performed revealed that the cooling rate in several media has significant effect on the microstructure of the weldment. Pearlite and ferrite have been noticed within the microstruc-ture, however the proportion of ferrite to pearlite diversified under totally different situations.

The procedure of weldability estimate, primarily based on the transformation diagrams of continuous cooling (CCT-diagrams) and the measured temperature cycles, is offered in this paper. The goal was to find out the weldability to have the ability to outline the optimum onerous-facing know-how of the thermo stable steels. The temperature cycles were measured and then the obtained values for the crucial cooling time t8/5 were entered into the CCT diagrams to estimate the hardness and microstructure of the welded joint’s zones. Experiments had been carried out on the multi-layered hard-faced samples manufactured from the steel for manufacturing of the forging dies.

For larger chilly forming quantities we advocate you to seek the advice of the metal producer prior to ordering. Hot forming of S690QL and other high yield steels just isn’t really helpful as the new forming will take away the advantages of the mills tempering process.

For constructional steelwork even plates of 120 mm have been produced and utilized efficiently particularly in bridges. The high yield energy of the bottom material must be taken into consideration when choosing the filler materials. It must be thought-about that elevated warmth enter leads to decrease tensile properties within the weld metal. If a stress relieving warmth treatment is planned throughout or after plate processing, this should also be thought of when choosing the filler materials.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.