St 690 Steel

S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Structural & Offshore Plates

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

In the circumstances of the overmatched welded joints containing a gentle root layer it’s possible to realize a comparable fracture behaviour related to the homogeneous overmatched welded joint if the impact toughness of the soft root layer is higher than the impact toughness of the overmatched weld metal. Such a type of welded joint is due to this fact preferable for the welding of excessive strength low alloy steels, as a result of it permits the manufacturing of a welded joint with out preheating. In this paper, the detailed procedure for defining the optimal technology for welding the constructions made of the high strength metal S690QL is introduced.

If a stress relieving heat remedy is deliberate during or after plate processing, this should even be thought of when choosing the filler materials. To avoid hydrogen-induced cold cracking, solely filler supplies, which add little or no hydrogen to the base metal, may be used. High power steels belong into a bunch of high quality steels, with exceptional mechanical properties, especially with reference to tensile power.

• This technique of cooling, often known as quenching, induces a metamorphosis within the crystalline structure of the steel which leaves it much harder.
• Unfortunately the metal on this situation is also very brittle and it isn’t attainable to use it in lots of functions.
• A method of warmth remedy for alleviating this drawback known as tempering and requires the quenched steel to be re-heated though this time to below the decrease critical temperature.
• It is feasible to produce metal plates that have more than twice the strength of these produced from delicate metal by way of a warmth remedy process known as quenching and tempering.
• Steel is heated to some extent above its higher critical temperature and is then in a short time cooled in water.

Unitedsteel Mill Supply High energy metal plate, and have numerous stock measurement, If you require excessive energy steel plate. Unitedsteel Mill Supply High strength steel plate, and have numerous inventory size, if you require excessive energy metal plate, please contact us by way of Email to contact us. S690Q is a hot-rolled hardened structural metal that has undergone subsequent tempering therapy and conforms to the EN , DSTU EN normal. To regain the preliminary properties new quenching and tempering turn out to be needed.

Rcyf Series Pipeline Permanent Magnet Iron Remover

It is able to improve the efficiency, durability, and security of vehicles, lifting gear, and metal buildings. Due to the steels high power, buildings can be designed lighter, payloads elevated, and energy used more efficiently.

In order to make sure that the tensile strength of the weld metallic fulfils the necessities of the bottom steel, the warmth enter and interpass temperature should be limited during welding. Experience has proven that the welding situations should be chosen in order that the cooling time t eight / 5 does not exceed 20 seconds.

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

mechanical properties of grade EN10025-6 S690Q

	Minimum yield strength – ReH MPa			Tensile strength Rm MPa			Minimum elongation – A Lo = 5,65* √So (%)
Steel grade	Nominal thickness mm			Nominal thickness mm
	>3 ≤50	>50 ≤100	>100 ≤150	>3 ≤50	>50 ≤100	>100 ≤150
S690Q	690	650	630	770-940	760-930	710-900	14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature °C		-20	0
Min. absorbed energy J		40	50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature °C	-40	-20	0
Min. absorbed energy J	27	30	35

The tables below show the chemical composition of grade EN10025-6 S690Q

	Ladle analysis. Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties. Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.
Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	B max. %	Nb max. %	V max. %	Ti max. %	Cr max. %	Mo max. %	Ni max. %	Cu max. %	Mo max. %	N max. %	Zr max. %	CEV max. %
																	≤50	>50 ≤100	>100 ≤150
S690QL	0,20	1,70	0,80	0,020	0,010	0,005	0,06	0,12	0,05	1,50	0,70	2,0	0,50	0,70	0,015	0,15	0,65	0,77	0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old EU 137 (1983)	France AFNOR	Sweden SS	Germany DIN,WNr
FeE 690 V KT	E690T	2625	TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

It is possible to provide steel plates that have more than twice the strength of those produced from delicate steel via a heat therapy course of known as quenching and tempering. Steel is heated to a point above its upper crucial temperature and is then very quickly cooled in water.

The metal is designed to provide excellent welding and bending properties and it provides substantial potentialities for savings in materials costs, processing and handing. Due to its excessive energy, it permits design of lighter, more sturdy and environment friendly products and buildings.

Sales@Victorsteels Com

S690ql High Yield Structural Steel

Our S690Ql is a structural metal grade and is produced to give high yield strength during usage. S690QL plates have greater payload capacity and are vitality environment friendly, hence can be utilized in leaner structures. This metal is used in other purposes such as heavy transportation, building EN10025-6 S690Q steel plate supplier business, machine constructing, and lifting gear. We deliver products in customizable choices to satisfy customer-specified requirements. Multipurpose Low-Carbon Steel Also known as gentle steel, multipurpose metal consists of low-carbon grades, such as 1018 and A36.

The second aspect is finding out the so-referred to as indirect corrosion, i.e. the corrosion of reinforcement throughout the strengthened concrete structural components, which might provoke corrosion of the concrete itself, its dropping out from structural element and thus reducing its structural integrity. S690QL STEEL PLATE GRADE AND SPECIFICATIONEN S690QL Steel Plates Due to the supplies excessive power nature, utilizing S690QL will promote leaner designed structures with elevated payload capacity and power effectivity. Finally, it’s the fabricator’s responsibility to acquire the required values of the steel via an appropriate heat remedy. If the temperature of 560 °C is exceeded, the preliminary tempering shall be altered in order that the mechanical properties are affected.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.