S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

The numerical values indicate that the maximum respective values of temperature measured in QT metal and TMCP metal were about 1300 and 1200 °C for a warmth enter of 10 kJ/cm, 1400 and 1300 °C for a heat enter of 14 kJ/cm, and 1600 and 1450 °C for a warmth input of 17 kJ/cm. The cooling times resulted, for a warmth enter of 10 kJ/cm, in numerical t8/5 (14.5 s) and experimental (18.84 s) increases in hardness within the coarse-grain warmth-affected zone of the QT metal (317 HV0.1), due to the formation of bainite and lath martensite buildings with grain progress. Decreased hardness in the CGHAZ of TMCP metal (240 HV0.1) was brought on by main recrystallization of the microstructure and the formation of more equilibrium merchandise of austenite decomposition. Increasing the warmth enter (14 to 17 kJ/cm) led to numerical t8/5 and experimental decreases in hardness within the CGHAZ of QT metal (270 HV0.1) because of the full austenite , and maintained the relative value of TMCP metal (235 HV0.1).

En10025

Based on the obtained outcomes an estimate was supplied relating to the weldability of S 960 QL metal as well as the proposal for additional research. The study evaluates numerically and experimentally the impact of welding warmth input parameters on the microstructure and hardness of the warmth-affected zone of quenched and tempered and thermo-mechanically managed course of 690-MPa excessive-strength steel. Numerical analyses and experimental comparisons had been utilized utilizing three heat enter values (10, 14, and 17 kJ/cm) to be able to predict the thermal fields during welding. Experimental analysis was carried out of the microstructure and microhardness habits in several HAZ areas.

• Gangsteel supply EN steel grade specification is a excessive yield strength structural steels in the quenched and tempered condition metal plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.
• We ship merchandise in customizable choices to satisfy buyer-specified necessities.
• This metal is used in other applications corresponding to heavy transportation, development business, machine constructing, and lifting equipment.
• Hot rolled merchandise of structural steels Technical delivery circumstances for flat merchandise of high yield power structural steels in the quenched and tempered condition of this doc, along with half 1, specifies necessities for flat products of excessive yield power alloy particular steels.

abs grade ah36 shipbuilding and offshore industries steel Has been dedicated to the of export metal business more than 10 years. Our service involves all kinds of steel product , together with uncooked supplies and processed finished merchandise. The procedure of plasticity-primarily based distortion analysis for directly mapping cumulative plastic strains into elastic fashions using equivalent thermal strains was developed and applied to the investigation of the characteristic relationship between cumulative plastic strains and angular distortion in fillet welded thin EN10025-6 S690Q steel plate supplier-plate T-joints. Plasticity-based distortion analysis successfully predicted the whole angular distortion with an accuracy of 97% compared with angular distortion obtained from the elastic-plastic analysis, demonstrating the validity of the unique relationship between cumulative plastic strains and distortions and the applicability of linear elastic models in welding-induced-distortion evaluation. The PDA procedure also supplied the quantitative relationship between six cumulative plastic pressure components and angular distortion of fillet welded T-joints.

If you need more yield power, you could choose our others grade in S690Q, S890Q or S960QS460QL,St37-2 steel equivalent – phare-stadsbrouwerijS460QL,As a metal supplier in China,we can supply St37-2 steel equal,boiler metal,Carbon metal,Weathering metal,Q345B steel,S355 metal,metal equal,any steel plate stock. ISO 630 specification for top yield energy structural steel plates,Fe360A,Fe360B,Fe360C,Fe360D,Fe430A,Fe430B,Fe430C,Fe430D,Fe510C,Fe510D.S620QL1,S550Q ,S550QL ,S550QL1, S500Q ,metal plate ,EN S620QL1,S550Q ,S550QL ,S550QL1, S500Q ,metal plate ,EN . EN metal grade specification is a excessive yield energy structural steels in the quenched and tempered condition metal plate grade in S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL metal plate grade.S620QL1,S550Q ,S550QL ,S550QL1, S500Q ,steel plate ,EN S620QL1,S550Q ,S550QL ,S550QL1, S500Q ,metal plate ,EN . EN steel grade specification is a excessive yield energy structural steels within the quenched and tempered condition steel plate grade in S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL metal plate grade.

The grades and qualities are given in Tables 2 to 4 and Tables 5 to 7 and are supplied within the quenched and tempered situation as given in 6.3. The steels specified on this doc are relevant to sizzling-rolled flat products with a minimal nominal thickness of 3 mm and a most nominal thickness ≤ 150 mm for grades S460, S500, S550, S620 and S690, a most nominal thickness ≤ 100 mm for grade S890 and a most nominal thickness ≤ 50 mm for grade S960, in steels which, after quenching and tempering, have a specified minimal yield energy of 460 MPa1) to 960 MPa1 ).

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

The unique conclusions on affect of the chosen welding process guide metal arc for the basis passes and metal energetic gasoline for the filling and covering passes) on impression toughness of the high-strength low-alloyed steels are drawn. The paper additionally presents dialogue on the valid requirements and suggestions associated to welding of these steels, from the aspect of functions in design of steel welded constructions.

Existing, very scarce and often unclear and inadequate suggestions for choice of the optimal welding know-how are one of the causes of large number of flaws in welded joints. Mentioned problems, as well as others, can be successfully solved by correct number of the procedure, filler metallic and know-how of welding, verified by experiments conducted in laboratory or in real operating situations.

S500ql Steel Plate Data Sheet Bebon Steel Top Steel Asme

S690QL High Strength Steel Plate Exporter, S690QL Structural Steel Plates Stockists in India, S690QL HSLA Plate, S690QL High Yield Steel Plate Supplier in Mumbai. As the plates production is done by making good use of optimum high quality of alloy, it tends to supply many good properties. As the plate’s manufacturing is completed by making good use of optimum high quality of alloy, it tends to offer many good properties. Those are excessive tensile power, toughness, weldability, excessive flexibility, sturdiness, longevity, withstanding heavy loads, good dimensional accuracy and fine floor finishes. Additionally, it is having a higher capability to be fully proof against corrosion, pitting, stress corrosion cracking, erosion, crevice corrosion, abrasion, and erosion and so on.

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

mechanical properties of grade EN10025-6 S690Q

	Minimum yield strength – ReH MPa			Tensile strength Rm MPa			Minimum elongation – A Lo = 5,65* √So (%)
Steel grade	Nominal thickness mm			Nominal thickness mm
	>3 ≤50	>50 ≤100	>100 ≤150	>3 ≤50	>50 ≤100	>100 ≤150
S690Q	690	650	630	770-940	760-930	710-900	14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature °C		-20	0
Min. absorbed energy J		40	50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature °C	-40	-20	0
Min. absorbed energy J	27	30	35

The tables below show the chemical composition of grade EN10025-6 S690Q

	Ladle analysis. Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties. Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.
Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	B max. %	Nb max. %	V max. %	Ti max. %	Cr max. %	Mo max. %	Ni max. %	Cu max. %	Mo max. %	N max. %	Zr max. %	CEV max. %
																	≤50	>50 ≤100	>100 ≤150
S690QL	0,20	1,70	0,80	0,020	0,010	0,005	0,06	0,12	0,05	1,50	0,70	2,0	0,50	0,70	0,015	0,15	0,65	0,77	0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old EU 137 (1983)	France AFNOR	Sweden SS	Germany DIN,WNr
FeE 690 V KT	E690T	2625	TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

Din17102 Tste380 Carbon And Low Alloy High Strength Steel

Our S690Ql is a structural metal grade and is produced to offer high yield energy throughout usage. S690QL plates have greater payload capacity and are energy environment friendly, therefore can be used in leaner structures.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.