S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

This will be possible without conducting the large variety of practical tests or relying on private expertise of a designer. Using excessive-strength thermomechanically rolled steel instead of regular structural steel grades substantially reduces the steel intensity of civil buildings as a result of the usage of columns with thinner partitions and flanges, yet the identical compression strength efficiency. For example, the usage of TMCP plates to make welded columns of recent industrial excessive-rise buildings permits 20-30% savings in rolled metal products. When used in open wagon buildings, TMCP plates make them lighter by 30-35%.

In order to ascertain the optimum welding process, one has to examine and/or confirm different parameters of the chosen technology. High energy steels belong into a gaggle of top quality steels, with distinctive mechanical properties, especially with reference EN10025-6 S690Q steel plate supplier to tensile power. At the identical time, as their deficiency is emphasised the restricted and difficult weldability. In other words, some of these steels are weldable solely with application of special measures associated to controlled heat enter.

A517gr E Pressure Vessel Steel Plate

The paper also presents discussion on the legitimate requirements and proposals related to welding of these steels, from the facet of applications in design of metal welded constructions. a hundred and fifty Amperes and different delicate steel electrode gauges of 10 and 12 have been investigated. The tensile energy, hardness and influence power of the welded joint have been carried out and it was found that the tensile power and hardness scale back with the increase in warmth enter into the weld. However, the influence energy of the weldment increases with the increase in warmth input.

Download Center

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

mechanical properties of grade EN10025-6 S690Q

	Minimum yield strength – ReH MPa			Tensile strength Rm MPa			Minimum elongation – A Lo = 5,65* √So (%)
Steel grade	Nominal thickness mm			Nominal thickness mm
	>3 ≤50	>50 ≤100	>100 ≤150	>3 ≤50	>50 ≤100	>100 ≤150
S690Q	690	650	630	770-940	760-930	710-900	14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature °C		-20	0
Min. absorbed energy J		40	50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature °C	-40	-20	0
Min. absorbed energy J	27	30	35

The tables below show the chemical composition of grade EN10025-6 S690Q

	Ladle analysis. Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties. Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.
Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	B max. %	Nb max. %	V max. %	Ti max. %	Cr max. %	Mo max. %	Ni max. %	Cu max. %	Mo max. %	N max. %	Zr max. %	CEV max. %
																	≤50	>50 ≤100	>100 ≤150
S690QL	0,20	1,70	0,80	0,020	0,010	0,005	0,06	0,12	0,05	1,50	0,70	2,0	0,50	0,70	0,015	0,15	0,65	0,77	0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old EU 137 (1983)	France AFNOR	Sweden SS	Germany DIN,WNr
FeE 690 V KT	E690T	2625	TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

This is particularly true for the TM steels since an S460M steel has a lower carbon equivalent than an strange structural metal. The TM steels have a wider window for warmth enter and preheating than QT steels. Even for thicker plates of S460M preheating can be omitted and thus welding prices decreased. It shouldn’t be uncared for that several other branches began with the applying of high power metal plate earlier.

Research Of Possibility For Improvement Of Welding Technology Of Microalloyed Steels

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

The grain structure of these plates relieves internal stress and imparts yield energy. The weldability of the plates is completed through standard welding strategies. However, these are welding of those plates is completed with out deforming. The plates exhibit superior machinability, subsequently these are drilled, forged, reduce and flanged with easy ease. Due to superior sporting properties these lowers the concern of harm to machinery and ensures the same wear performance for each use.

The usually accepted situations for the energy overmatched welded joints of high energy metal are not clearly defined. In this paper, the fracture mechanics evaluation of specimens, with surface notch suggestions completely embedded in the warmth affected zones was carried out. The outcomes showed that the strength of mismatching of a welded joint caused a redirection of the crack propagation in the direction of the low strength region of the welded joint.

This implies that the hot fashioned plate will then must be tempered again. Given that a lot of the power of the plate comes from the optimised tempering process any advert hoc tempering is prone to result in quote completely different results than those of the initial plate.

Consequently the MTC won’t mirror the precise properties of the metal. input on the mechanical properties of the welded joint the test steels had been welded with one, two or more runs, out of which samples have been made for the production of specimens to be able to measure the hardness and impact strength in HAZ .

• In this paper, the detailed procedure for outlining the optimum know-how for welding the buildings made from the excessive strength metal S690QL is offered.
• The most prominent properties are the excessive tensile power and impression toughness, at room and at elevated temperatures, as well.
• That metal belongs into a group of steels with exceptional mechanical properties.

Experimental tensile testings of the specimens were performed at 5 different temperatures within the range from 20 to 550°C. Beside experimental testing, strengthening curves have been calculated and numerical evaluation using finite factor technique was carried out.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.