En 10025

S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

These are processed from the heat treatment course of, sizzling working and annealing process. However, the cold working operation is most well-liked essentially the most to strengthen plates with none embrittlement and corrosion. They are exposed to greater temperatures to achieve larger service in decreasing zones. After manufacturing, these plates are processed for finishing operation the place uneven surfaces are eliminated by the commercial finishing course of.

The manufacturing of the plates is finished under the very strict supervision of the professionals’ experts that are having good years of working expertise and wanted EN10025-6 S690Q steel plate supplier skills. In compliance with various uncooked material high quality standards and business norms, the production is made effective.

High Strength Steel Plate

The research evaluates numerically and experimentally the effect of welding heat enter parameters on the microstructure and hardness of the heat-affected zone of quenched and tempered and thermo-mechanically managed course of 690-MPa high-strength metal. Numerical analyses and experimental comparisons were applied using three warmth enter values (10, 14, and 17 kJ/cm) to be able to predict the thermal fields throughout welding. Experimental analysis was carried out of the microstructure and microhardness habits in different HAZ areas. The numerical values indicate that the utmost respective values of temperature measured in QT metal and TMCP metal had been about 1300 and 1200 °C for a heat enter of 10 kJ/cm, 1400 and 1300 °C for a heat input of 14 kJ/cm, and 1600 and 1450 °C for a warmth enter of 17 kJ/cm.

High Yield Strength Steels

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

mechanical properties of grade EN10025-6 S690Q

	Minimum yield strength – ReH MPa			Tensile strength Rm MPa			Minimum elongation – A Lo = 5,65* √So (%)
Steel grade	Nominal thickness mm			Nominal thickness mm
	>3 ≤50	>50 ≤100	>100 ≤150	>3 ≤50	>50 ≤100	>100 ≤150
S690Q	690	650	630	770-940	760-930	710-900	14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature °C		-20	0
Min. absorbed energy J		40	50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature °C	-40	-20	0
Min. absorbed energy J	27	30	35

The tables below show the chemical composition of grade EN10025-6 S690Q

	Ladle analysis. Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties. Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.
Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	B max. %	Nb max. %	V max. %	Ti max. %	Cr max. %	Mo max. %	Ni max. %	Cu max. %	Mo max. %	N max. %	Zr max. %	CEV max. %
																	≤50	>50 ≤100	>100 ≤150
S690QL	0,20	1,70	0,80	0,020	0,010	0,005	0,06	0,12	0,05	1,50	0,70	2,0	0,50	0,70	0,015	0,15	0,65	0,77	0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old EU 137 (1983)	France AFNOR	Sweden SS	Germany DIN,WNr
FeE 690 V KT	E690T	2625	TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

This redirection of the crack propagation affected the values of the critical CTOD. Such a kind of welded joint is subsequently preferable for the welding of excessive energy low alloy steels, as a result of it permits the manufacturing of a welded joint with out preheating.

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

It must be considered that increased heat enter results in decrease tensile properties within the weld metallic. If a stress relieving heat therapy is planned throughout or after plate processing, this should also be considered when deciding on the filler materials. To avoid hydrogen-induced cold cracking, solely filler supplies, which add very little hydrogen to the base metallic, could also be used.

Mobile crane building uses today metal grades up to a yield stress of 1100 MPa; within the offshore trade thermo-mechanically rolled steels in higher energy courses are prone to be the metal group the most typically used for cold water purposes. The production of the S690QL – ESSAR PLATES is finished through the use of premium high quality of alloy that is actually sourced from reliable market vendors. The materials right here is heat handled the tempering and quenching process and is having excellent welding and ending properties.

That consists of verifying the chemical composition of the delivered base steel, determining its weldability, deciding on the type of eventual heat therapy and then checking that the executed welded joints possess the required mechanical and metallurgical properties. In this paper, the detailed procedure for defining the optimal know-how for welding the structures made from the excessive power steel S690QL is presented.

S690ql Steel Plates, S690ql Quenched & Tempered Steel Plates, En 10025 S690ql Plates Stockists In Mumbai, S690 Plate, En 10025

• At the identical time, as their deficiency is emphasised the restricted and troublesome weldability.
• High strength steels belong into a group of top quality steels, with exceptional mechanical properties, especially with regard to tensile power.
• We deliver products in customizable choices to fulfill buyer-specified necessities.
• In different phrases, a few of those steels are weldable only with application of particular measures associated to controlled heat input.

The steels treated right here have low contents of alloying elements and low carbon equivalents. They may be easily welded to all odd structural steels utilizing any typical arc welding method. This is particularly true for the TM steels since an S460M steel has a lower carbon equivalent than an ordinary structural metal. The TM steels have a wider window for warmth enter and preheating than QT steels. Even for thicker plates of S460M preheating could be omitted and thus welding prices lowered.

We aim to contribute within the growth to led monetary efficiency and results in growing a value for our shoppers. Under the surveillance and steering of professionals, we turn out to be one the largest trader and stockholder of heavy responsibility ferrous and non-ferrous plates. We are making these plates in numerous standards, specs, designations, and non-normal dimensions. With trending manufacturing facility and tools, we’re capable of obtain products with larger precision and dimensional accuracy.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.