S690Q Standard: EN 10025-6:2004, European standard for hot-rolled structural steel. Part 6 – Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

Aisi 4118 Alloy Steel (Uns G Azom

Gangsteel produced and export EN10025-6 high strength S690Q steel plate, We had min 1000tons stock for high strength S690Q equal grade and we also provide the cutting service with cnc, water cutting or laser cutting. Related keywords:en s690q,en 10025 s690ql,en 10025-6 s690q,en 10137 2 grade s690q,en 10025-6 s690ql equivalent astm,s690ql en 10025,s690q en 10025-6,en 10025 s690ql1,s690q en 10137-2,en 10137-2 s690ql,s690ql en 10025-6,en 10025 s690q,en 10025 steel,en 10025-s355j2men 10025-2 s355jr,en 10025 astm equivalent,en 10025-6 s690ql,en 10025 s690ql,en 10025 steel equivalent,en 10025 s355k2g4,en 10025-6 s690ql equivalent astm,en 10025-6 s690q,bs en 10025-6-s690ql,acero en 10025-6 s690ql,en 10025 s690ql1,en 10025 p 6 2004 s690ql,en 10025-1 equivalent,ss-en 10025-6 s690ql and en 10025-6 grade s690ql.

EN S690QL Plates are made in India and include an EN .1 MTC. Laser beam welding and laser-arc hybrid welding are anticipated to be applied to welding of excessive-power steel plates over 780 MPa, as a result of they have advantages similar to low distortion and a slender warmth-affected zone. This research examined the connection between the chemical composition of high-strength metal plates and the microstructure and mechanical properties of the weld metal with the purpose of enhancing the toughness of welded joints of excessive-power steels by the LBW process. The outcomes revealed that weld metallic toughness is strongly dependent on the carbon content of the metal plates, and wonderful toughness can be obtained in weld metals with low C contents having an virtually fully lower bainite construction with out formation of slender martensite austenite constituent . Based on these results, a tenet for applicable alloying factor design for high-strength steels for LBW was proposed, targeting mechanical properties of tensile power ≥980 MPa and toughness vE−forty °C ≥ 47 J.

Manusteelcnchina Steel Suppliers Superior Technology

The method was utilized to S355 structural steel bulk samples in addition to an autogenously electron beam welded pattern the place there is a local variation of material properties. Applying the brand new technique to indentation knowledge from completely different areas of an S355 steel weld and utilizing this knowledge as an enter into an FE model of the cross-weld, tensile data from the FE model resulted matching the experimentally measured properties to within 5%, confirming the efficacy of the brand new inverse evaluation approach. aluminum sheet aluminum sq. tube 0.25 in metal stock bar steel stock three/4 solid metal pipe flat beam RELATED PRODUCTS 1-half in. In the paper the results of metallographic examination and mechanical properties of electron beam welded joint of quenched and tempered steel grade S690QL are presented.

EN 10025-6 S690Q-strength 1045 carbon steel

The tensile energy of joint was larger than the base steel and the fracture occurred on the base steel. The weld hardness was significantly higher than the bottom steel, the bending energy was 1300 MPa, which was better than base metal, and the bending strength elevated slightly with beam current. The bending angle of joint was fifty four°, which was barely decrease than the base metal. The current work is targeted on monitoring the microstructure evolution of the thermomechanically rolled medium-C metal containing Si and Al to stop precipitation of carbides.

  • In practice, engineering materials corresponding to structural steels, titanium alloys and high power aluminium alloys are multi-part metals with microstructural length scales that can be the identical order of magnitude as the maximum achievable nano-indentation depth.
  • Based on these results, a suggestion for acceptable alloying component design for prime-energy steels for LBW was proposed, targeting mechanical properties of tensile power ≥980 MPa and toughness vE−40 °C ≥ forty seven J.
  • The outcomes revealed that weld steel toughness is strongly dependent on the carbon content material of the metal plates, and excellent toughness can be obtained in weld metals with low C contents having an almost absolutely lower bainite construction without formation of slender martensite austenite constituent .
  • This research examined the connection between the chemical composition of high-energy metal plates and the microstructure and mechanical properties of the weld metallic with the purpose of bettering the toughness of welded joints of excessive-strength steels by the LBW process.

Many more dislocations and plastic deformations were found in the fusion zone than the heat-affected zone in the joint, which hardened the joints and lowered the impression toughness. The microstructures characterized by FTEM–power-dispersive X-ray spectrometer also exhibited laths of M, as well as stacking faults and dislocations that includes high-density, interfacial structure EN10025-6 S690Q steel plate supplier ledges that happen between the high-angle grain boundaries and the M and bainite. A537 steel plate is right for each in boilers and stress vessels, and is used in the oil, gasoline and petrochemical trade.The ASTM A537 specification covers heat handled carbon metal plates for stress vessel functions.

DIN EN S690Q /S690QL/S690QL1 Condition of Delivery Water quenched and tempered. Typical Applications Heavy road vehicleschassis, dumper bodies. Cranes constructionbooms of mobile cranes. Structural steelworksbridges, bridge components, components for offshore structures. Pressure vesselsfixed and transportable storage tanks, vessels.S690Q Steel Plates Manufacturer in China, S690Q Steel The S690Q grade is austenitic in nature suitable for heavy engineering works. Plus, it has good formability and weldability property. Plates are both magnetic and non magnetic in nature. It serves good resistivity towards crevice and pitting cracking subjected to impact loads.S690QL Plate, S690QL Steel Plates, S690QL Quenched and What is S690QL Steel Plate Legally certified industry Rexton steel & alloys are busy in supplying the excellent and desirable quality of S690QL PLATES globally. They are fully focusing on offering clients with the top notch quality of plates and other essential services.

S690Q steel is used in structures subject to extreme loadsmining and heavy construction equipment, crane equipment, offshore drilling platforms, supporting structures for wind turbines, bridges and trestles.Plates of S690Q steel grade MetinvestS690Q structural high strength steel with minimum yield strength of 690 MPa supplied in quenched and tempered condition (Q). Plates of S690 steel grade comply with EN 10025 6 standard.S690Q / 1.8931 SteelNumber Chemical composition S690Q Number1.8931 ClassificationAlloy special steel with specified minimum values of impact energy at temperatures not lower than 20 °C StandardEN 10025 62004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition

The primary role of that circumstances is related with automobile body material, welding technology, state of stress and temperature. Because of that, a good selection of metal and welding methodology is essential for correct metal construction. Low alloy metal is used for automotive physique construction, very often with small amount of carbon and the amount of alloy elements corresponding to Ni, Mn, Mo, Cr and V in automobile physique and welded joints. Depending on the sort of metal which is used, a proper welding technique and enough filler materials must be applied.

无标题文档

S690Q is stunning yield quality real steels review in the quenched and tempered. The picture S is relating steel, 690 for the base yield quality in thickness under 50mm.The Symbol Q mean the vehicle condition in secured and tempered. S690q could be through the 20-temperature impact and the significance is 30J.Definition of BS7608 fatigue classes for structural steels Concerning the oxy fuel cutting, the Loga mean test values of S355M and S690Q are lower than the corresponding Loga limit values obtained for the design class B, so class B cannot be applied strictly to S355M and S690Q with oxy fuel cut edges. Consequently, the analysis followed here provides the same fatigue class for oxy fuel cut straight Down Loadstone Supplier.Gangsteel supply high strength steel plates in S690Q,S690QL,S690QL1,S890Q,S960Q,S890QL
Equivalent Grades of EN 10025–6:2004 S690QL Steel Plate

Grade

Standards

Country

S690QL EN10137-2 EN10025-6:2004

EN

EUROPE

A709-100

ASTM

USA

TStE690V DILLIMAX 690 NAXTRA 70

DIN, WNr

GERMANY

E690T E690TFP S690T

AFNOR/ NF A36- 204

FRANCE

FeE690VKT

EN

EUROPEAN (OLD)

2625 WELDOX 700

SS

SWEDON

E690

ISO 4952

INTER

JFE HITEN 780LE

JIS

JAPAN

ALFORM 700

AUSTRIA

mechanical properties of grade EN10025-6 S690Q

 

Minimum yield strength – ReH
MPa

Tensile strength Rm
MPa

Minimum elongation – A
Lo = 5,65* √So (%)

Steel grade

Nominal thickness
mm

Nominal thickness
mm

 

>3
≤50

>50
≤100

>100
≤150

>3
≤50

>50
≤100

>100
≤150

S690Q

690

650

630

770-940

760-930

710-900

14

EN10025-6 Notch impact test.
Notch impact test – longitudinal. Minimum values of impact energy for impact tests on longitudinal V-notch test pieces for quenched and tempered steel

EN10025 S690Q Structural Steel. EN10025:6:2004 Hot Rolled S690Q, Steel Number 1.8928. 690 N/MM 2 high yield, high strength structural steel plate notch impact tested in longitudinal direction to the rolling direction at 40degree C, thus being excellent in forming and Pharmacia ita welding properties that achieve another higher level of beauty and durability in steel engineering structure. Steel Plate 2.25Cr1Mo0.25V(H) S690QSteel Plate 2.25Cr1Mo0.25V(H) Category Pressure Vessel and Boiler Steel Plate ModelWYJ046 2006 Standard Specification is for boilers and pressure vessels designed in H2 service. The dimension, shape, weight and permissible deviation shall comply with SA20/SA20M.Optimal welding technology of high strength steel S690Q For the S690Q L steel, the recommended . preheating temperature should be 150

Temperature
°C

-20

0

Min. absorbed energy
J

40

50

Notch impact test – transverse. Minimum values of impact energy for impact tests on transverse V-notch test pieces for quenched and tempered steel, when the impact test on transverse test pieces is agreed at the time of the order.

Temperature
°C

-40

-20

0

Min. absorbed energy
J

27

30

35

The tables below show the chemical composition of grade EN10025-6 S690Q

 

Ladle analysis.
Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties.
Nb, Ti, V, Zr shall be at least 0,015 % of a grain-refining element present. Aluminum is also one of these elements. The minimum content of 0,015 % applies to soluble aluminum, this value is regarded as attained if the total aluminum content is at least 0,018 %; in case of dispute the soluble aluminum content shall be determined.

Steel grade

C
max.
%

Mn
max.
%

Si
max.
%

P
max.
%

S
max.
%

B
max.
%

Nb
max.
%

V
max.
%

Ti
max.
%

Cr
max.
%

Mo
max.
%

Ni
max.
%

Cu
max.
%

Mo
max.
%

N
max.
%

Zr
max.
%

CEV
max. %

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

≤50

>50
≤100

>100
≤150

S690QL

0,20

1,70

0,80

0,020

0,010

0,005

0,06

0,12

0,05

1,50

0,70

2,0

0,50

0,70

0,015

0,15

0,65

0,77

0,83

 

EN10025-6 S690Q Steel Grade Equivalent Table

European old
EU 137 (1983)

France
AFNOR

Sweden
SS

Germany
DIN,WNr

FeE 690 V KT

E690T

2625

TStE690V

Description by Manufacturer
Sell: S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1, Steel plate, EN 10025-4
EN 10025-6 steel grade specification is a high yield strength structural steels in the quenched and tempered condition steel plate grade in S500QL, S500QL1, S460Q, S460QL, S460QL1, S620QL1, S550Q, S550QL, S550QL1, S500Q, S890QL1, S960Q, S960QL, S620Q, S620QL, S690Q, S690QL, S690QL1, S890Q and S890QL steel plate grade.

1. Steel Grade : S690Q, S690QL, S690QL1, S890Q, S890QL, S890QL1, S960Q, S960QL, S620Q, S620QL, S620QL1, S550Q, S550QL, S550QL1, S500Q, S500QL, S500QL1, S460Q, S460QL, S460QL1.

2. Dimension(T*W*L) : Thickness: 6mm to 300mm ; Width: 1500mm to 4020mm ; Length: 4000mm to 18000mm

3. Adopt Standard: EN 10025-6.

4. Heat Treatment:
Hot Rolled, CR, Normalized, Quenched, Tempering, TMCP, Electroslag Remelting Technical.

5. Steel Services: Cutting, Painting, Ball blast, Pretreatment and the Third party in section in DNV, BV, LR, GL, ABS and CCS in super thick ship steel plate

6. Payment Item: 30% TT, or LC and TT

7. Trade Terms: FOB, CFR, CIF

8. Delivery Time: 30-40days

However, the traditional welding produces a relatively broad weld that contributes to the deterioration of mechanical properties. Though the impairment of the mechanical performance of welds can’t be avoided and fully eliminated, it may be decreased by producing a very narrow warmth affected zone that adjoin to the weld.

The temperature sequence of the precipitation underneath equilibrium conditions was decided. The Dutta-Sellars mannequin has been utilized for determination of recrystallization stop temperature of austenite and time needed for Nb precipitation.

Double-facet welding technique permits better weld penetration and higher control of heat distribution. Observation of the samples confirmed that the fusion zone exhibited bainitic and martensitic microstructures with increased amounts of martensites in contrast with the bottom supplies. Also, the grains within the fusion zone increased in coarseness as the heat input was elevated. The fusion zone exhibited increased hardness (397 HV0.2) while exhibiting a simultaneous decrease in the impact toughness. The maximum impact energy value of 26 J was obtained from the single-facet-welded sample, which is larger than these obtained from the double-aspect-welded samples .

The chemical composition of AISI 4118 alloy steel is outlined within the following table. We supply excessive grade s890ql steel plate at affordable value. These s890ql metal plate are manufactured using most interesting grade uncooked materials out there to make sure worldwide quality. These s890ql steel plate are available in several form size and thickness in accordance with the wants of our buyer. S890QL1 meets the necessities of EN for the corresponding grades.

Our S690Q is a structural steel grade and is produced to give high yield strength during usage. The material can be heat treated using quench and temper techniques. These EN 10025 6 Plates have good forming and welding properties. S690Q plates have higher payload capacity and are energy efficient, hence can be used in leaner structures.S690Q / 1.8928 SteelNumber Chemical composition Nominal thickness = 50(mm) CEV max = 0.65 Nominal thickness from 50 to 100 (mm) CEV max = 0.77 Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified propertiesEN 10025 S690QL Brown McFarlaneHigh strength quenched and tempered steel plate can be easily welded and fabricated. We often find that steel plate to EN 10025 S690QL is called different things by different engineers. Plate to this specification and grade is variously described asHigh Strength Quenched and Tempered Steel Plate. If you have requirement for high strength steel plate,please contact us by email.