astm a240 gr 316l

Gangsteel are the large stainless steel supplier. our main Grade A240 316L A240 SS316L, A240 TP316L A240 Type 316L aisi 316L Stainless plate, SQ pipe, cutting parts, Stainless disc and angle.a240 316l stainless,aisi 316l stainless steel,a240-316l 7days delivery time,a240-316l cutting parts,a240 316l machined parts,316l stainless steel astm,316/316l stainless steel,316l 316 H beam.

316l stainless plate

Grade 316 can be topic to stress corrosion cracking above around 60°C. 316/316L Stainless Steel Sheet, is a well-liked grade of stainless where superior corrosion resistance is of primary importance.

Stainless steel plate A240 316L

  1. What ASTM A240 Type 316L
    A240 316L is a grade of stainless steel, AISI 316L is the corresponding American grade, and sus 316L is the corresponding Japanese grade.

The unified digital code in my country is S31603, the standard brand is 022Cr17Ni12Mo2 (new standard), and the old brand is 00Cr17Ni14Mo2, which means that it mainly contains Cr, Ni, and Mo, and the indicates the approximate percentage. The national standard is GB/T 20878-2007 (current edition).

  1. What a240 316L density?  The a240 316L density is 7.98g/cm3;
  2. What is A240 316L yield?
    Tensile strength σb (MPa): ≥480

Conditional yield strength σ0.2 (MPa): ≥177
Elongation δ5 (%): ≥40
Reduction of area ψ (%): ≥60
Hardness: ≤187HB; ≤90HRB; ≤200HV
Density: 7.98g/cm3;
Specific heat capacity ratio (20℃): 0.502J/(g*K)

Steel Grade

Mechanical Property

ASTM(A240M)

Others(JIS)

Tensile Properties

Hardness

Bend Test

Yield StrengthMPa

Tensile StrengthMPa

Elongation%

HBW

HRBW

316

SUS316

≥205

≥515

≥40

≤217

≤95

316L

SUS316L

≥170

≥485

≥40

≤217

≤95

316H

 

≥205

≥515

≥40

≤217

≤95

Gangsteel relative keywords.
A240 316l|A240 aisi 316l|A240 ss316l|A240 sus 316l|A240 316l steel|A240 316l surgical steel|A240 1.4404 stainless steel|A240 316l ss|A240 316l stainless|A240 tp 316l|A240 316l stainless steel price|A240 316 316l|A240 316 stainless tubing|A240 sa 240 316l|A240 1.4404 steel|A240 astm a312 tp 316l|A240 s31603|A240 aisi 316l stainless steel|A240 a312 tp 316l|A240 astm 316l|A240 er 316 l|A240 316l stainless steel price per kg|A240 gr 316|A240 din 1.4404|A240 316l stainless steel pipe|A240 sa240 316|A240 astm a312 tp 316|A240 316l grade stainless steel|A240 astm a240 316l|A240 1.4435 stainless steel|A240 a240 316l|A240 astm 316 stainless steel|A240 316l stainless steel tubing|A240 1.4404 stainless|A240 316l stainless steel sheet|A240 sa 240 gr 316|A240 316 stainless rod|A240 metal 316l|A240 316 stainless sheet|A240 316 stainless plate|A240 316l sst|A240 ss 1.4404|A240 316l stainless steel plate

  1. What astm a240 316l equivalent?

EQUIVALENT ASTM A240

No

JIS G4304

ASTM

UNS

KS

EN10095

AS

CNS

10

SUS309S

309S

S30908

STS309S

1.4833

309S

309S

11

SUS310S

310S

S31008

STS310S

1.4845

310S

310S

12

SUS316

316

S31600

STS316

1.4401

316

316

13

SUS316Ti

316Ti

S31635

1.4571

316Ti

316Ti

14

SUS316L

316L

S31603

STS316L

1.4404

316L

316L

15

SUS316N

316N

S31651

STS316N

316N

316N

16

SUS316LN

316LN

S31653

STS316LN

1.4429

316LN

316LN

17

SUS316J1

STS316J1

316J1

316J1

18

SUS316J1L

STS316J1L

316J1L

19

SUS317

317

S31700

STS317

317

317

20

SUS317L

317L

S31703

STS317L

1.4438

317L

317L

  1. What does a240 mean? A-240 Heat-Resisting Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels. SA-263 Corrosion-Resisting Chromium Steel Clad Plate, Sheet, and Strip.

Grade

ASTM A240 316L Chemical Composition

ASTM(A240M)

Others(JIS)

C

Si

Mn

P

S

Ni

Cr

Mo

Others

316

SUS316

≤0.08

≤0.75

≤2.00

≤0.045

≤0.030

10.0/14.0

16.0/18.0

2.00/3.00

N≤0.10

316L

SUS316L

≤0.030

≤0.75

≤2.00

≤0.045

≤0.030

10.0/14.0

16.0/18.0

2.00/3.00

N≤0.10

316H

0.04/0.10

≤0.75

≤2.00

≤0.045

≤0.030

10.0/14.0

16.0/18.0

2.00/3.00

Gangsteel other products
A240 316 stainless pipe|A240 a240 316|A240 316l grade surgical steel|A240 astm a240 316|A240 316l surgical stainless steel|A240 316l tube|A240 sa 312 tp 316l|A240 grade 316l|A240 titanium 316l|A240 sae 316l|A240 316l pipe|A240 316l surgical grade stainless steel|A240 sae 316l stainless steel|A240 astm a479 316|A240 tp 316|A240 1.4404 aisi 316l|A240 sa 479 316l|A240 sa 240 gr 316l|A240 sa 240 tp 316l|A240 316l|A240 type 316l stainless steel|A240 316 and 316l|A240 aisi 1.4404|A240 steel 1.4435|A240 sus 316l stainless steel|A240 sa 213 tp 316l|A240 astm 316l stainless steel|A240 ss316l pipe|A240 316l plate|A240 ss316 and ss316l|A240 aisi 316l ss|A240 astm a312 gr tp316l|A240 316l austenitic stainless steel|A240 sa 240 tp 316|A240 a276 316l|A240 astm a269 tp316|A240 316 sheet|A240 a269 tp316|A240 astm a240 tp 316|A240 316l astm|A240 316 stainless bar|A240 cres 316l|A240 316l 1.4404 stainless steel|A240 316 and 316l stainless steel|A240 316l stainless steel hypoallergenic|A240 316 stainless round bar|A240 a240 tp316l|A240 astm a240 tp316l|A240 ss 316l grade|A240 316 stainless flat bar|A240 stainless steel grade 1.4404|A240 304 316l|A240 sst 316l

  1. A240 304 VS A240 316l SAE 316L, What is different of 304 AND 316L?
    Essentially, Grade 304 is an austenitic chromium alloy which is also known as an "18/8" stainless as the make-up of the steel is 18% chromium and 8% nickel. The chromium content promotes the material’s considerable resistance to the effects of corrosion and oxidation.
    The two most commonly used stainless steels 304 and 316L (or 1.4308 and 1.4408 corresponding to German/European standards). The main difference in chemical composition between 316 and 304 is that 316L contains Mo, and it is generally recognized that 316L has better corrosion resistance.

It is more corrosion resistant than 304 in high temperature environment.
Therefore, in high temperature environments, engineers generally choose 316 material components.

A240 316L is commonly used in chemical and petrochemical industry, in food processing, pharmaceutical equipment, medical devices, in potable water, wastewater treatment, in marine applications and architectural applications near the seashore or in urban areas.

 

While 316 isn’t fully rust-proof, the alloy is extra corrosion-resistant than other common stainless steels. It is the preferred steel to be used in marine environments due to its larger resistance to pitting corrosion than different grades of steel. The proven fact that it is negligibly responsive to magnetic fields signifies that it can be utilized in applications the place a non-magnetic metallic is required. In addition to molybdenum, 316 additionally accommodates numerous Stainless steel plate supplier other components in various concentrations. Like different grades of chrome steel, marine grade stainless steel is a relatively poor conductor of each warmth and of electricity when in comparison with metals and different conductive materials. All frequent hot working processes may be carried out on 316 stainless-steel. Post-work annealing is really helpful to make sure optimum corrosion resistance.

  • They are a comparatively low stainless product and utilized in quite a lot of purposes.
  • 316 stainless-steel plate grades have good welding characteristics and submit weld annealing is not normally required to revive efficiency.
  • 316 and 316L stainless steel plates are part of the austenitic family of stainless steel and they are one of the versatile and widely used kinds of stainless plate.
  • 316 grades have excellent low temperature properties and reply well to hardening by chilly working.

Austral Wright Metals assumes no legal responsibility in connection with the knowledge on this Product Data Sheet. Austral Wright Metals provides a complete vary of stainless steels, alloys, nickel alloys and different excessive performance metals for difficult service circumstances. Our engineers and metallurgists shall be pleased to provide further data and applications recommendation. Another method of manufacturing stainless steel plate inside and beyond the thickness range of coil manufacturing is from a slab of steel that’s rolled within the flat condition to a specified size, width and thickness.

A240 316l stainless steel surface finish plate stockist

Gangsteel supply the stock stainless steel plate. A240 316L OR SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron, are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), with small (<1%) quantities of silicon, phosphorus & sulfur also present. The addition of molybdenum provides greater corrosion resistance than 304, with respect to localized corrosive attack by chlorides and to general corrosion by reducing acids, such as sulfuric acid. 316L grade is the low carbon version of 316 stainless steel. When cold worked, 316L can produce high yield and tensile strengths similar to Duplex stainless grades.

The strength or endurance limit is the utmost stress beneath which materials is unlikely to fail in 10 million cycles in air surroundings. For austenitic stainless steels as a group, the fatigue power is typically about 35 percent of the tensile energy. Substantial variability in service outcomes is skilled since extra variables corresponding to corrosive situations, form of stress and imply worth, floor roughness, and other factors have an effect on fatigue properties. For this reason, no definitive endurance limit values can be given that are representative of all working circumstances. At temperatures of about 1000°F (538°C) and better, creep and stress rupture turn out to be considerations for the austenitic stainless steels.

CompositionComposition Ranges for 316 grade of stainless steels Sheets & Plates. ~ Low thermal conductivity of austenitic alloys leads to heat concentrating at the slicing edges. This means coolants and lubricants are necessary and have to be utilized in large quantities. Type 316L is a variant of Type 316 and differs by having a lower Carbon content material in addition to slightly decrease yield and tensile strengths. Type 316L offers improved and in addition reduces the potential for lower corrosion resistance round welded areas. Improved Machinability – This plate offers better machinability than commercially produced chrome steel plate. Possible alternative grades to grade 316 stainless steels are given in table 5.

Gangsteel production range for stainless, our max thickness 300mm, the max width 2600mm. Thickness 3mm to 300mm. 316/316L steel has outstanding corrosion resistant properties, whether it is atmospheric or oxidizing environment, even for marine atmosphere, it shows excellent corrosion resistance in welded state. Normally 316/316l steel shows no magnetic in condition, cold drawn or cold rolling process may make it with little magnetic, and it can be fixed with further processing.

A240 316l stainless plate price|A240 316l stainless steel plate properties|A240 316l stainless steel plate price per kg|A240 316l stainless steel plate weight|A240 316/316l plate|A240 plate 4 mm 316l|A240 316l tread plate|A240 ss 316l plate unit weight|A240 316l stainless steel plate mechanical properties|A240 316l stainless steel plate specifications|A240 316l stainless steel plate thickness|A240 ss 316l plate density|A240 ss 316l plate price in india|A240 ss 316l plate weight|A240 316l plate suppliers|A240 316l plate weight|A240 316l plate |A240 316l plate price|A240 ss 316l plate chemical composition|A240 aisi 316l plate|A240 cres 316l plate|A240 316l diamond plate|A240 ss 316l plate weight calculator|A240 a240 316l plate|A240 astm 316l plate|A240 316l plated stainless steelA240 ss 316l plate|A240 316l ss plate|A240 316 stainless plate|A240 316l stainless steel plate|A240 316l stainless plate|A240 316l plate specification|A240 316l stainless steel plate price|A240 316l steel plate|A240 ss 316l plate rate

astm a240 316l

A240 316l stainless steel price per pound|A240 sa 240 type 316l|A240 aisi 316l steel|A240 316l round bar|A240 a4 316l|A240 a240 gr 316l|A240 ss 316l pipe price|A240 1.4404 ss|A240 316l din|A240 asme 316|A240 cf3m 316l|A240 316 stainless angle|A240 sandvik 316l|A240 316l 316ti|A240 astm a479 316l|A240 316l sheet|A240 316 surgical stainless steel|A240 a213 tp316l|A240 spj 316l|A240 ss316 ss316l|A240 316l 2b|A240 1.4432 stainless steel|A240 316l marine grade stainless steel|A240 type 316l|A240 sa316l|A240 a312 316|A240 aluminium 316l|A240 ss 316 and 316l|A240 aws 316l|A240 ss316l stainless steel|A240 tp316l stainless steel pipe|A240 sa 479 gr 316|A240 316l stainless steel pipe supplier|A240 s31603 sst|A240 a358 316l|A240 astm a213 tp316l|A240 astm a240 type 316l|A240 a240 tp 316|A240 316 seamless tubing|A240 sa 249 316l|A240 ss 316l sheet price|A240 316l ug|A240 1.4435 aisi 316l|A240 a 312 tp 316l|A240 316l plate|A240 316 plate

316 and 316L stainless-steel plates are a part of the austenitic family of stainless steel and they are some of the versatile and broadly used kinds of stainless plate. They are a relatively low value stainless product and used in quite a lot of applications. 316 grades have glorious low temperature properties and respond well to hardening by cold working. 316 chrome steel plate grades have good welding characteristics and publish weld annealing is not normally required to revive performance.

A240 316l stainless steel vs 925 sterling silver plate stockist

Alloy 2507 with 4% Mo, 25% Cr, and 7% Ni is designed for use in salt water. The Alloys 316 and 317L are thought of to be adequate for some marine setting functions corresponding to boat rails and hardware and facades of buildings close to the ocean, that are uncovered to salt spray. The Alloys 316 and 317L stainless steels all carry out without evidence of corrosion in the a hundred-hour, 5% salt spray check. Grade 316 has excellent corrosion resistance when uncovered to a range of corrosive environments and media. It is usually thought to be “marine grade” stainless-steel but isn’t resistant to warm sea water.

316l stainless plate

A240 42mm 316l stainless steel plate stockist

The molybdenum offers 316 stainless steel plate better total corrosion resistant properties than grade 304 chrome steel plate. It has notably greater resistance to pitting and crevice corrosion in chloride environments. 316 chrome steel plate has wonderful forming and welding characteristics. Grade 316 chrome steel plate additionally has outstanding welding traits. Grade 316L chrome steel plate is the low carbon model of 316 stainless steel plate and is extensively used in heavy gauge welded elements.

316 stainless-steel plate is comprised of at most 0.08% carbon while 316L stainless-steel plate solely accommodates up to 0.03% carbon. 316 and 316L stainless steel plate both are composed of not more than 2.0% manganese, 0.75% silicon and 0.045% phosphorous. Both 316 and 316L contain at most 0.03% sulfur, between 16.00% and 18.00% chromium, and between 2.0% and 3.0% molybdenum. 316 and 316L chrome steel plate also incorporates between 10.0% and 14.0% nickel and not more than 0.10% nitrogen. Alloy 316/316L resists atmospheric corrosion, as well as, moderately oxidizing and decreasing environments.

Contact Us
HENAN GANG IRON AND STEEL CO.,LTD
Email: admin@gangsteel.com
Phone: whatsapp: 0086-13598879167

CN CHINA
, ,

Yes, it’s possible to purchase twin certified stainless steel plate in grades 316 and 316L. The main benefit of using 316and 316L chrome steel plate over 304 and 304L chrome steel plate is it’s usually extra proof against corrosion. Because 316 and 316L stainless steel plate contains extra chromium and molybdenum, it holds up better beneath corrosive environments and in marine functions. 316 is likely one of the simpler austenitic stainless steels to forge, at temperatures above 925°C. In most applications the steel is used where its corrosion resistance offers lengthy lasting service life and appearance. The ease of cleaning and of maintaining a hygienic surface on the metal make it excellent for a lot of purposes. This alloy has wonderful resistance to atmospheric and chemical corrosion.

A240 316l stainless steel vs grade 5 titanium plate stockist

Gangsteel had 3000tons raw stock material and we can produce A240 316L Stainelss steel plate with faster delivery time. 7-10days we can be ready for delivery. If you have inquiry for 316L stainless steel material, please contact us.

316l stainless plate
Tagged on: